Lijian Pan
材料科学技术（英文）
The composite laminates with embedded acrylonitrile butadiene rubber (NBR) layer were fabricated by cocuring process. The embedded layers were perforated with a series of small holes to allow resin to flow through the damping layer and completely couple the structure to improve bending stiffness and interlaminar shearing strength of these cocured composite laminates. The damping, bending stiffness and shearing strength of these composite laminates with different perforation diameters were investigated. The experimental results show that increasing the perforation diameter leads to significant decreases in damping and significant increase in bending stiffness up to an area ratio of 7.065%. The area ratio here is defined as the ratio of perforation area to the total damping area. Beyond the area ratio of 7.065%, increasing the diameter to an area ratio of 50.24% results in only a slight variation in damping and bending stiffness. Moreover, increasing the perforation diameter does not always increase the shearing strength of the embedded viscoelastic layer. The shearing strength of embedded viscoelastic layer increases only when the area ratio is greater than 19.625%; instead, it will decrease.
关键词:
Composite laminates
,
null
,
null
,
null
,
null
Lijian Pan
材料科学技术（英文）
Presented herein is a methodology for the multi-objective optimization of damping and bending stiffness of co-coured composite laminates with embedded viscoelastic damping layer. The embedded viscoelastic damping layer is perforated with a series of small holes, and the ratio of the perforation area to the total damping area is the design variable of the methodology. The multi-objective optimization is converted into a single-objective problem by an evaluation function which is a liner weigh sum of the two sub-objective functions. The proposed methodology was carried out to determine the optimal perforation area ratios of two viscoelstic layers with different perforation distance embedded in two composite plates. Both the optimal perforation area ratios are approximate to 2.2%. However, the objective value of the plate with greater perforation distance in embedded viscoelatic layer is much greater.
关键词:
Composite laminates
,
null
,
null
,
null
L.Ren
,
K.Tsuru
,
S.Hayakawa
,
A.Osaka
材料科学技术（英文）
Several gelatin-silicate composites, with or without incorporation of Ca2+ ions, were synthesized through set-gel processing starting from gelatin and 3- (glycidoxypropyl) trimethoxysilane. The structure around the Si atoms was similar for all the samples. The measurement of viscoelastic properties indicated that the glass transition temperature and activation energy decreased with the incorporation of Ca2+ ions. The Ca2+ ion-containing composites were bioactive as they spontaneously deposited apatite when soaked in a simulated body fluid of the Kokubo recipe.
关键词:
Mingshi SONG and Jincai YANG (Research Institute of Polymeric Materials
,
Beijing University of Chemical Technology
,
Beijing
,
100029
,
China)Yiding SHEN(North West Institute of Light Industry
,
Shanxi Xianyang
,
712087
,
China)
材料科学技术（英文）
It is shown theoretically that the viscoelasticity of polymer melts is determined by three combining factorst they are the primary molecular weight and its distribution, the number of entanglement sites on polymer chain and the sequence distribution of constituent chains in entanglement spacings. A unified quantity for the three combing factors is the average constrained dimensional number of constituent chains in the long entanglement spacings (v). A new relation of v to the primary molecular weight and the number of testing polymers were derived from the multiple entanglement and reptation model, and a new method for determining v was proposed. The dependences of linear viscoelastic functions on the primary molecular weight and its distribution were derived by the statistical method. When Mn=6Me to 18 Me, the values of (v) can range from 3.33 to 3.70. Their values are in a good agreement with the experiment data, and it can slightjy vary with the different species of polymers and the different ranges of molecular weight of polymers
关键词: