Author S.R. Zhou
,
S.R. Qiao
,
S.H. Bai and C.S. Tian Faculty 401
,
Northwestern Polytechnical University
,
Xian 710072
,
ChinaManuscript received 18 October 1998
金属学报(英文版)
The tensile properties of three different carbonfiberreinforced carbon composites (C/C), mat C/C, 2D laminate and 4D C/C, were investigated under the combined influence of temperature and loading rate. From the experiments the following could be concluded: loading rate between 10-1-10 mm/min was valid; the fracture stress of the three kinds of C/C composites increased with increasing temperature in the range from room temperature to 1900, and the initial modulus of 2D laminate C/C composites increased with the increase of temperature up to 2000.
关键词:
tensile testing
,
null
,
null
,
null
张贵华
,
董洪波
,
朱深亮
,
刘诚
材料热处理学报
TC4-DT钛合金经高温恒应变速率变形后,进行三重热处理,具体工艺为:(920～960℃)×1 h水冷(WQ)+ (880 ～920)℃×1h WQ+ 820℃×1.5h空冷(AC),观察热处理后的微观组织.结果表明:TC4-DT钛合金950℃变形后,第一重热处理温度越高,初生等轴α相含量越少,在温度为920℃时由等轴α相、针状α'相及β基体组成,960 ℃时等轴α相完全消失;第二重热处理中,初生α相有减少的趋势,温度越高,减少越快.第二重热处理温度对次生条状α相含量及最终形态也有影响,当二重热温度为920 ℃时得到的条状α组织更为粗大;经过第三重热处理,条状α相的间距均匀,在条状一次次生α相之间分布有更加细小的二次次生α相.因而采用不同条件的多重热处理制度可以调节材料的微观组织,包括次生α的长度、宽度及次生α片层的数量等,从而可以优化TC4-DT钛合金的微观组织.TC4-DT钛合金950℃高温变形后,经960℃×1 h WQ+ 880℃×1 h WQ+ 820℃×1.5 h AC热处理,得到细小均匀的网篮组织;经940℃×1 h WQ +920℃×1 h WQ+ 820℃×1.5 hAC热处理,得到双态组织.
关键词:
TC4-DT钛合金
,
高温
,
拉伸
,
热处理
,
微观组织
李晓源
,
时捷
,
董瀚
材料研究学报
用定量金相、扫描电镜和能谱分析等方法获取了用2种工艺冶炼的40CrNi2Mo钢中夹杂物尺寸特征参数,研究了这些参数对钢塑性的影响.结果表明:由于夹杂物的体积分数和尺寸比较小,夹杂物间距的增大,在塑性断裂时由夹杂物形成的微孔洞很难以内颈缩形式聚合,微孔洞间的局部剪切也不容易扩展.由此判断,真空自耗重熔钢的断面收缩率比电渣重熔钢的高.钢中的夹杂物对其均匀延伸率、形变硬化指数和拉伸强度没有影响.
关键词:
金属材料
,
超高强度钢
,
拉伸实验
,
40CrNi2Mo钢
,
塑性
,
夹杂物