Z.L. Mi
,
D. Tang
金属学报(英文版)
he influence of cold rolling reduction on microstructure and mechanical properties of the TWIP (ttwinning induced plasticity) steel was investigated. The results indicated that the steel had better comprehensive mechanical properties when cold rolling reduction was about 65.0% and the annealing temperature was 1000℃. The tensile strength of the steel is about 640MPa and the yield strength is higher than 255MPa, while the elongation is above 82%. The microstructure is composed of austenitic matrix and annealing twins at room temperature, at the same time, a significant amount of annealing twins and stacking faults are observed by transmission electron microscopy (TEM). Mechanical twins play a dominant role during deformation, and result in excellent mechanical properties.
关键词:
cold rolling reduction
,
rolling
,
reduction
,
annealing
,
tempera
Weimin MAO
材料科学技术（英文）
The effects of pouring temperature, short electromagnetic stirring with low strength and then soaking treatment on the microstructure of AlSi7Mg alloy were investigated. The results show that if AlSi7Mg alloy is poured at 630 or 650℃ and meanwhile stirred by an electromagnetic field at a low power for a short time, the pouring process can be easily controlled and most solidified primary α-Al grains become spherical and only a few of them are rosette-like. Weak electromagnetic stirring makes the temperature field more homogeneous and makes the primary α-Al grains disperse in a larger region, which leads to the spherical microstructures of primary α-Al grains. When the AlSi7Mg alloy is soaked or reheated at the semisolid state, the primary α-Al grains ripen further and they become more spherical, which is favorable to the semi-solid forming of AlSi7Mg alloy.
关键词:
AlSi7Mg alloy
,
alloy
,
semi-solid
,
pouring
,
tempera