A novel technology to prepare styrene-butadiene rubber (SBR)/carbon nanotubes (CNTs) composites was developed by combining a spray drying method and a subsequent mechanical mixing process. The cross-linking degrees of the vulcanized composites increased gradually with the additive CNTs contents. By comparing with those of the pure SBR composites, the mechanical properties such as tensile strength, tear strength and hardness of the composites filled with CNTs at certain contents were dramatically improved almost by 600%, 250% and 70%, respectively. The fabrication of the CNTs filled with SBR composites by combination of the spray drying method and subsequent mechanical mixing process was effective for enhancing the reinforcement
effects of CNTs in rubbers. The novel technology can also open a new route for the modification and reinforcement on the nanocomposites with large amount of CNTs.
关键词:
Carbon nanotubes
,
styrene-butadiene rubber
,
spray drying
,
mechanical mixing
,
nanocomposite
,
mechanical property
李彩霞
,
任瑞晨
,
满东
,
张乾伟
,
程强
,
程明
,
庞鹤
硅酸盐通报
通过化学成分分析、粒度分析、X-射线衍射、SEM分析等方法,对吉林某矿区的煤矸石的性质进行了研究,并对煤矸石进行化学改性,利用改性后的煤矸石部分代替炭黑作橡胶补强材料,制品的拔出力均高于国标和企业标准,并对其进行了补强机理分析.
关键词:
煤矸石
,
丁苯橡胶
,
化学改性
,
补强填料
武卫莉
,
虞文品
绝缘材料
以硅橡胶（MVQ）为基相，以团状模塑料为增强相，以丁苯橡胶（SBR）为相容剂制备了DMC/SBR/MVQ绝缘复合材料，研究了SBR的用量对MVQ性能的影响及混合方式和硫化条件对复合材料性能的影响。结果表明：通过SBR和MVQ共混制得的并用胶性能优于纯MVQ和DMC/MVQ的性能，DMC、SBR、MVQ最佳配比为60∶25∶75；其最佳的混炼方式是将MVQ和SBR分别进行混炼，白炭黑和DMC分批加入；最佳硫化条件为：温度180℃，压力1.2 MPa，时间15 min，制备的复合材料的体积电阻率大于4.9×1012Ω·m，SBR的加入提高了DMC/MVQ绝缘复合材料的性能。
关键词:
甲基乙烯基硅橡胶
,
丁苯橡胶
,
团状模塑料
,
绝缘复合材料
,
共混
,
性能
涂春潮
,
王珊
,
任玉柱
,
蒋洪罡
,
黄艳华
航空材料学报
doi:10.3969/j.issn.1005-5053.2014.2.011
通过热捏合方法制备SE2045/SBR共混胶并利用RPA2000分析共混胶在不同温度、频率、应变下的性能.结果表明,在SE2045阻尼硅橡胶中并入10％的SBR,可以将SE2045阻尼硅橡胶的拉伸强度提高28.4％,达到10.58MPa,撕裂强度提高260％,达到51.6 kN/m;但共混胶的工艺性能不如SE2045阻尼硅橡胶.加入10％的SBR后,SE2045阻尼硅橡胶的模量及阻尼性能提高,但材料性能随温度、频率的变化趋势不变;在应变为1％ ～ 20％范围内,SE2045/SBR共混胶阻尼性能tanδ随应变的增加先降低后升高,而SE2045的阻尼性能先降低后趋于平稳.
关键词:
硅橡胶
,
丁苯橡胶
,
共混
,
模量
,
阻尼
林路
,
古菊
,
谢东
,
罗远芳
,
贾德民
复合材料学报
采用固相法制备了玉米淀粉接枝马来酸酐(MAH)和苯乙烯(St)的共聚物Starch-g-MAH-St (SMS).采用机械共混法制备了接枝改性淀粉/丁苯橡(SMS/SBR)复合材料,研究了复合材料的力学性能、热空气老化性能、动态力学性能以及微观形态.结果表明,SMS/SBR复合材料的力学性能优于未改性淀粉/SBR复合材料和纯SBR.当苯乙烯和MAH单体用量都为原淀粉质量的10%且SMS的用量为20 g/100 g SBR时,SMS/SBR复合材料的力学性能最佳.经100℃热空气老化48 h后,复合材料的拉伸强度仍可达10 MPa.与纯SBR硫化胶相比,SMS/SBR复合材料的玻璃化转变温度(T_g)降低.微观形态分析显示,淀粉经改性后粒子尺寸减小,在SBR中的分散性得到了改善,与SBR基体的相容性得到了提高.
关键词:
淀粉
,
接枝改性
,
固相法
,
丁苯橡胶
,
复合材料
,
性能
傅应才
,
王勇
,
张峰
高分子材料科学与工程
doi:10.16865/j.cnki.1000-7555.2016.12.020
为研究铺地材料对丁苯胶(SBR)熔融流淌燃烧行为的影响,文中选取了瓷砖、钢板、聚氯乙烯(PVC)地板革和石膏板4种铺地材料,在自行搭建的实验平台上进行燃烧实验,获得了质量、液池及池火面积、温度场等数据.分析表明,4种铺地材料上丁苯胶(SBR)液池扩展速率、池火蔓延速率、燃烧速率及火焰温度从大到小的顺序均为:钢板＞石膏板＞PVC地板革＞瓷砖,基本与铺地材料的热容大小顺序(瓷砖＞石膏板＞PVC地板革＞钢板)相反,其中PVC地板革裂解产物的阻燃性进一步降低了其燃烧速率.此外,由于其良好的导热性,钢板对燃烧的流淌熔体的熄灭作用随时间先增大后减小,SBR燃烧速率后期出现快速增长,表现出非线性特点.
关键词:
丁苯胶
,
熔融
,
流淌燃烧
,
池火
,
铺地材料