JIANG Qichuan HE Zhenming CHEN Yanping Jilin University of Technology
,
Changchun
,
China.
材料科学技术(英文)
The abrasive wear behaviour of austenitic medium manganese steels was studied under weak corrosion-abrasive wear simulating the liner plate in wet metallic ore bail mill under non-severe impact-loading working condition. Results show that the work-hardening mechanism and the wear resistance of high carbon austenitic medium manganese steels differ from those of medium carbon austenitic medium manganese steel. Under non-severe impact and weak corrosion-abrasive wear,the wear resistances of high carbon and medium carbon austenitic medium manganese steels are 50-90% and 20-40% higher than that of Hadfield steel respectively.
关键词:
carbides
,
null
,
null
,
null
徐勇
,
张士宏
,
程明
,
宋鸿武
,
王苏程
金属学报
doi:10.3724/SP.J.1037.2012.00769
研究了不同温度范围单向拉伸加载方式对奥氏体不锈钢力学性能和组织演变的影响.结果表明,循环加卸载拉伸方式显著影响304不锈钢的力学性能:在高温拉伸变形时,不同加载方式所得到的力学性能相同;在0℃以下,循环加卸载方式导致试样的延伸率降低;而在室温条件下,循环加卸载拉伸能够最大程度地提高试样的强度和延伸率.通过对304不锈钢室温拉伸过程的原位观测证实,卸载过程导致能够有效激发形变诱发马氏体相变的形核和长大,从而使相变增塑效应增强,延迟缩颈及断裂的能力得以提高.
关键词:
奥氏体不锈钢
,
加载方式
,
循环加卸载拉伸
,
形变诱发马氏体
,
相变增塑效应
陈孟
,
黄俊霞
,
叶晓宁
材料热处理学报
设计了一组不同成分的低镍铬锰氮奥氏体不锈钢,通过热轧、退火、冷轧及Gleeble热模拟,观察研究了实验钢在不同状态下的显微组织、力学性能及高温热变形行为的变化规律.结果表明:热轧后实验钢的强度随固溶温度的提高而降低,塑性随固溶温度的提高而增大,实验条件下的最佳固溶温度为1050℃;冷加工变形量的增大能显著提高显微组织中形变马氏体的含量,增大实验钢的强度、硬度和屈强比,降低断后伸长率,且在实验范围内抗拉强度与维氏硬度在数值上呈现近似3倍的关系.热加工过程中实验钢的易裂敏感区间约为750 ~950℃,最佳热加工区间为1000 ~1200℃.
关键词:
低镍奥氏体不锈钢
,
亚稳态
,
形变诱导马氏体
,
加工硬化