非晶态Fe_(90-x)Si_xZr_(10)(x=0,4,7,10)合金是用单辊急冷方法制备的,用提拉样品磁强计测量了样品的磁化曲线和热磁曲线。发现每个磁性原子的平均磁矩μ和Curie温度T_c随Si含量的增加而增加,与相应的非晶态FeSiB合金相比,非晶态FeSiZr合金的μ和T_c明显偏低,认为这一反常现象是Fe-Fe原子间的反铁磁耦合的存在所致。低温下样品的磁化强度与温度的关系较好地符合Bloch T~(3/2)定律,得到自旋波劲度系数D从x=0时的0.37meV·um~2增加到x=10时的0.538meV·um~2,计算出交换相互作用范围都是在最近邻原子间的距离。
关键词:
非晶态
,
magnetic moment
,
Curie temperature
,
spin wave excitation
SHEN Baogen ZHANG Zhiying GUO Huiqun ZHAO Jiangao Institute of Physics
,
Academia Sinica
,
Beijing
,
ChinaGU Benxi Nanjing University
,
Nanjing
,
China
金属学报(英文版)
The magnetization curves at 1.5 K and thermomagnetic curves for amorphous Fe_(90-x)Si_xZr_(10)(x=0,4,7 and 10)alloys prepared by the drum spinning technique have been measured with an extracting sample magnetometer.It is obtained that the average magnetic moment,,per magnetic atom and Curie temperature,T_c,in the amorphous FeSiZr alloys increase with increasing Si content.The and T_c are found to be quite small,compared with amorphous FeSiB alloys.This unusual behavior is suggested to be due to the presence of the Fe—Fe antiferromagnetic interactions.The temperature dependence of magnetization at lower temperature is in accordance with Bloch's T~(3/2) law.Calculation shows that the spin wave stiffness constant,D,increases with increasing Si content from 0.37 meV·nm~2 for x=0 to 0.538 meV·nm~2 for x=10.The values ofindicate that the range of the exchange interaction is roughly the mean atomic distance of nearest neighbours.
关键词:
amorphous FeSiZr alloys
,
null
,
null
,
null