The microstruetural transformation of steels:20SiMn2V,20SiMn2VRE,40SiMn2V and 40SiMn2VRE during quenching and tempering have been examined by TEM,X-ray diffraction and dilatometer.It was shown that the addition of rare earth metals not only can refine the austenite grains of the low or medium carbon steels and packet of lath martensite and lath size,lower the M_s temperature,but can also raise the relative percentage of disloca- tion substructure of martensite in medium carbon steel,but there is little effect on volume frac- tion and thermal stability of retained austenite quenching and tempering structure of low or medium carbon steels.The rare earth metals may remarkably inhibit the decomposition of low carbon martensite during low temperature tempering,retard the precipitation of cementite plates in lath grains and delay the spheroidization of carbides.They may also restrain obvious- ly the precipitation and spheroidization of cementite in medium carbon martensite during high temperature tempering.
关键词:
rare earth metals
,
null
,
null
,
null
高妍
,
陈文琳
,
郭震
,
王梁
材料热处理学报
采用慢应变速率拉伸试验、晶间腐蚀和剥落腐蚀试验、硬度和电导率测试、光学显微镜等分析方法,研究微量(0.15 mass%)稀土对7085铝合金(Al-7.5Zn-1.5Mg-1.4Cu-0.15Zr)强度和腐蚀性能的影响.结果表明,与未添加稀土的铝合金相比,添加微量(0.15 mass%)稀土使7085铝合金组织细化,时效后强度、硬度提高,电导率略有降低,抗晶间腐蚀、剥落腐蚀和应力腐蚀性能显著提高.
关键词:
7085铝合金
,
稀土
,
晶间腐蚀
,
剥落腐蚀
,
应力腐蚀
陈宇昕
稀土
概述了国内外氟化物熔盐电解制取稀土金属及合金的发展历程,分析总结了实验室中对稀土氟化物熔盐体系研究,其中包括物化性质和电化学性质的研究.数值模拟技术近年来在熔盐电解法制备稀土金属中也起到了很大的作用,因此概述了数值模拟技术在熔盐电解制备稀土金属的发展.
关键词:
氟化物体系
,
电解法
,
稀土金属
,
研究历程
蔺广森
,
戴红
,
常仕英
,
赵云昆
,
王亚明
,
杨冬霞
贵金属
通过离子交换法以分子筛为原料进行稀土元素Ce的改性,并负载贵金属Pd制备出整体式催化剂材料,利用对比实验考察了改性分子筛的孔结构、储氧量、低温碳氢吸附活性、台架储氧能力和催化活性。采用低温氮吸附(BET)、程序升温还原(TPR)、台架性能测试(AFR)和台架储氧能力(OSC)进行了表征。结果表明,改性分子筛在比表面积、孔容上有所下降,但是提高了催化剂低温碳氢的吸附活性、台架储氧能力、储氧量和催化活性。
关键词:
物理化学
,
分子筛
,
改性
,
稀土
,
催化
,
离子交换