金属学报
本文研究了8090Al—Li合金的点蚀、晶间腐蚀和剥落腐蚀性能,探讨了热处理制度对耐腐蚀性能的影响。结果表明:Al-2.79Li-1.3Cu-0.7Mg-0.12Zr合金自然时效态抗晶间腐蚀和剥落腐蚀性能最佳,峰时效状态耐腐蚀性能最差,欠时效比过时效略好。显微组织观察表明合金的耐蚀性能与显微组织密切相关,峰时效条件下,粗大T_2相连续分布于晶界上,它的电位比基体电位低因此晶界构成阳极通道,从而使合金耐蚀性能恶化。
关键词:
Al-Li合金
,
pit corrosion
,
intergranular corrosion resistance
,
exfoliation behaviour
ZHANG Yun
,
LIU Yulin
,
ZHAO Hong' en
,
HU Zhuangqi
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
ChinaZHU Zhiyong
,
WANG Zhengfu
,
Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
China ZHANG Yun
,
Associate Professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
The A1-2.79Li-1.3Cu-0.7Mg-0.12Zr(8090) alloy has excellent resistance to intergranular and exfoliation corrosion as naturally aged, worst as peak aged and rather better as underaged than as overaged. The corrosion behaviour of the alloy is closely dependent on its microstructure. Under the peak aging condition, the coarse T_2 phase, which is continuously distributed along grain boundaries, has so low corrosion potential in comparison with the ma- trix, this makes the corrosion resistance of the alloy to be deteriorated by anodic dissolution along grain boundaries.
关键词:
AI-Li alloy
,
null
,
null
,
null
于香利
,
沈全锋
,
罗双全
,
储勇
,
刘军
腐蚀与防护
doi:10.11973/fsyfh-201511018
某水泵站项目中出现不锈钢管道腐蚀问题.对管线母材和焊缝材料进行了成分分析和微观分析,发现焊缝处耐蚀合金含量低于母材处,腐蚀主要发生在焊缝处.对腐蚀机理进行了探讨,水中的氯离子含量高是导致腐蚀的主要原因,现场温度高是次要原因.根据现场实际情况,对腐蚀处采用BELZONA高分子材料进行修复,有效解决了不锈钢的腐蚀问题,保证了管道的正常运行.
关键词:
1.4301不锈钢
,
点蚀
,
腐蚀机理
,
BELZONA
,
修复
白新德
,
彭德全
,
贺非
,
尤引娟
,
王瑞偏
,
陆金发
,
苏亲善
稀有金属材料与工程
测量A0纯铝在去离子水中的极化曲线用来模拟反应堆池壳的点蚀.研究表明:A0纯铝在去离子水中很容易钝化.实验中用美国EG&G普林斯顿应用研究公司生产的273型恒电位/恒电流仪测量模拟孔电位,极化曲线表明:模拟腐蚀坑处于钝化状态,即便是氧化膜破裂,腐蚀坑也发展得很慢.用pH计测量孔中pH的变化,并得到其工作曲线,此曲线表明:带有氧化膜的点蚀坑坑内存在明显的酸化现象.并对A0铝池壳的服务寿命进行了估计.
关键词:
点蚀
,
A0纯铝
,
模拟
,
阳极极化
,
电极电位
,
酸化
冯绍彬
,
李振兴
,
胡芳红
,
孙喜莲
电镀与涂饰
结合金属小孔腐蚀机理,分析了金属镀层腐蚀的特点,给出了提高镀层耐蚀性能的途径,如多层镍工艺,光亮Ni/Cr镀层工艺,打底镀层,镀后处理等.
关键词:
金属镀层
,
小孔腐蚀
,
耐蚀机理