研究了20CrNiMo钢微氮渗碳层中残余奥氏体的形态,及其在疲劳断裂过程中的转变和作用。结果表明:渗碳层残余奥氏体有薄膜状和块状两种形态,由于界面取向的影响,疲劳裂纹更易于穿过块状奥氏体,促使其发生应变诱发马氏体相变。在疲劳断裂过程中,裂纹面附近的残余奥氏体大部分转变成马氏体,这种转变是在断裂瞬间发生的,与疲劳力学条件无关。转变所引起的体积膨胀增强了裂纹闭合效应。相变诱发闭合是渗碳表层高碳区疲劳裂纹扩张行为的主要因素之一。
关键词:
残余奥氏体
,
fatigue crack growth
,
strain induced martensite transformation
,
phase transformation induced crack closure
JING Xiaotian LOU Bingzhe GU Chenqing SHEN Fusan Shanxi Institute of Mechanical Engineering
,
Xi'an
,
China Dept.of Materials
,
Shanxi Institute of Mechanical Engineering
,
Xi'an 710048
,
China
金属学报(英文版)
The morphology of the retained austenite in the carburized case of 20CrNiMo steel and its transformation during fatigue crack propagation through the case were investigated by using X-ray and TEM analysis.In the carburized case both film and block shaped retained austenite were found.Due to the crystallographic orientation relationship at the interface,the fatigue crack is inclined to pass through the block shaped retained austenite and thereby stim- ulates its strain-induced martensitie transformation.During the process of the fatigue frac- ture,most of the retained austenite structures on the crack path are transformed into the martensite,and the untranaformed parts on the fracture surface remain less than 6%.The transformation of the retained austenite,which is restrieted mainly within the plastic zone,oc- curs only during the proeess of fracture,and is independent of the magnitudes of the external stress,stress ratio and cyclic number.The volume expansion accompanying the transforma- tion creates an additional residual displacement of about 0.44μm on fracture surfaces,which is equivalent to the magnitude of the plasticity-induced residual displacement.The phase transformation induced fatigue crack closure is believed to be an important factor affecting the fatigue crack behaviors in the high carbon laver of the carburized case.
关键词:
retained austenite
,
null
,
null
,
null