Xuemei GUO
,
Kun LUO
,
Nanlin SHI
材料科学技术（英文）
In the presence of p-toluene sulfonic acid (TSA) as a dopant, polyaniline (PAni) nanofibers, (about 80~165 nm in diameter) were successfully synthesized with a chemical template-free method. It was found that the formation probability, morphology, and diameter of the resulting PAni-TSA nanofibers were sensitive to the synthetic conditions, such as reaction temperature, the molar ratio of TSA to aniline, and the concentration of TSA in the polymerization media. The molecular structure was characterized by using the FT-IR, Raman spectra and X-ray diffraction, which shows that the main chain structure of PAni-TSA nanofibers was in agreement with that of granular PAni.
关键词:
Polyaniline
,
null
,
null
,
null
张文娟
,
李铁虎
,
卢萌
,
侯翠岭
新型炭材料
doi:10.1016/S1872-5805(13)60073-6
实验制备了三种改性煤沥青,分别是:用苯丙烯醛(CMA)改性的沥青,用对甲苯磺酸(PTS)改性的沥青,以及用上述这两种物质混合改性的沥青.通过红外光谱及热分析对原料沥青及改性沥青进行了表征.对这四种沥青在不同温度下进行炭化,并对其炭化产物进行红外光谱和偏光表征.结果表明,通过改性,煤沥青的性能和炭化行为发生较大变化.在这四种沥青中,用CMA和PTS混合物改性的沥青,炭化产率高于仅用其中一种物质改性的沥青的炭化产率.另外,100 g煤沥青用7 gPTS和10 mL CMA的混合物改性的产物在800℃的炭化产率比原料沥青增加5.08％.并且在相同条件下,与其他三种沥青相比,其能够得到更多的中间相碳微球.红外光谱结果表明,在改性沥青热解过程中,CMA在300℃以下挥发,并且甲基和亚甲基随着温度的升高逐渐消失.
关键词:
煤沥青
,
苯丙烯醛
,
对甲苯磺酸
,
炭化
李建辉
,
卫世乾
合成材料老化与应用
本实验以冰乙酸和环己醇为原料,对甲苯磺酸为催化剂合成乙酸环己酯,通过正交实验考察了醇酸物质的量比、催化剂用量、反应时间等因素对酯化率的影响.结果表明,当冰乙酸的加入量为0.1mol,醇酸物质的量比为1.6∶1,催化剂用量0.2g,反应时间2h的条件下,酯化率可达97％以上.所得产品无色透明,通过红外光谱分析对产品进行了结构表征.
关键词:
乙酸环己酯
,
对甲苯磺酸
,
正交设计
,
催化合成