通过在18,35和55℃蒸馏水中疲劳裂纹扩展试验,证明了超高强度钢30CrMnSiNi2A腐蚀疲劳具有强烈的温度效应,得到了ΔK值和温度对裂纹扩展速率影响的复合表达式。由于扩展速率数据拟合得到的表观激活能值(36.7kJ/mol)十分接近于氢在γ-Fe中的扩散激活能值,支持了氢助裂纹扩展的观点。对大气中疲劳裂纹扩展具有重要价值的过载迟滞效应,在腐蚀疲劳时显著地减小,在0.1Hz的低频率下尤其明显。
关键词:
腐蚀疲劳
,
crack growth rate
,
temperature effect
,
overload retardation effect
QIAN Yourong HE Xiangdong Beijing University of Aeronautics and Astronautics
,
Beijing
,
China QIAN Yourong
,
Dept.of Materials Science and Engineering
,
Beijing University of Aeronautics and Astronautics
,
Beijing 100083
,
China
金属学报(英文版)
The fatigue crack growth rate (CGR) of ultra high strength steel 30CrMnSiNi2A in distilled water at 18,35 and 55℃ were measured.It was confirmed that the temperature is strongly af- fected on the corrosion fatigue CGR of ultra high strength steel.An expression concerning the effects of Δ K and temperature on the CGR was proposed.The fact that the apparent activation energy (36.6 kJ/mol) resulted from regressive analysis of CGR data was similar to the activation energy of hydrogen diffusion in γ-Fe,strongly supporting the theory of hydrogen-assisted crack growth.The overload retardation effect was greatly reduced in cor- rosion fatigue crack growth,especially at lower frequency,e.g.,0.1 Hz.This phenomenon might be due to the increase of the SCC component of CGR after an overload.
关键词:
corrosion fatigue
,
null
,
null
,
null