研究了Ti_3Al-Nb合金在高温下的有序化,冷却过程高温β相转变及时效过程亚稳定β相分解的行为,结果指出,在1060℃固溶处理时,合金形成初生α_2和β高温有序相;在固溶处理后的冷却过程中,合金发生β→α_2+ω型转变;在700℃时效过程中,合金发生(β+ω型)亚稳→(α_2+β)稳定分解。
关键词:
Ti_3Al-Nb合金
,
ordering transformation
,
α_2
,
β
,
ω
LI Dong ZHOU Jing CHANG Xin GUAN Shaoxuan Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China
金属学报(英文版)
Study was made of the behaviour of ordering transformation in Ti_3AI-Nb alloy,including the ordering at high temperatures,the transformation of high temperature β-phase during cooling,and the decomposition of metastable β-phase during aging.The results show that the ordered primary α_2 and high temperature β in alloy form at 1060℃.The transformation of high temperature β-phase proceed by β→α_2+ω type during cooling,and the decomposition of metastable β and ω type proceeded by(β+ω)_(metustabte)→(α_2+β)_(stable)during aging at 700℃.
关键词:
Ti_3Al-Nb alloy
,
null
,
null
,
null
,
null
孙峰
,
李金山
,
寇宏超
,
罗文忠
,
刘向宏
,
冯勇
稀有金属
研究了近α型Ti60钛合金自β单相区连续冷却至室温过程的相转变规律,冷却速率控制在80℃.s-1至0.1℃.s-1范围内.采用膨胀法原位分析了冷却过程中β→α '马氏体转变和β→α扩散型转变的起止温度及动力学特征,并观察对比了不同冷却速率下显微组织特征.在超过50℃·s-1的快冷条件下,原始β目约在910℃快速转变为细小针状α'马氏体,并且没有残余.在马氏体内部发现大量的位错以及(1011)层错,证明转变过程伴随有晶格畸变.在5℃·s-1的慢冷条件下,a相在β晶内和晶界都有形核,而在低于1℃·s-1时,α相仅在晶界形核,透射电镜下发现a片层间仍残留少量β相,而在片层内部α相发生了有序转变,形成α2相.冷却速率决定了连续冷却过程中同素异构的相转变机制以及生成相的内部结构.
关键词:
膨胀法
,
近α钛合金
,
冷却速率
,
α'马氏体
,
有序化转变
毕珺
,
张昆华
,
王传军
,
谭志龙
,
张俊敏
,
管伟明
,
宁远涛
贵金属
运用DSC、XRD、SEM/EDS、力学性能测试及电学性能测试对TO-5微型继电器触点用新型Au基六元合金AuCuPtPdNiRh的物相组成和时效行为进行了细致研究。结果表明，合金由晶格常数分别为0.3915和0.3827 nm的2种立方相组成；时效热处理并不改变2种相的形貌及元素构成；通过一次时效可使合金硬度和强度分别达到440和1458.4 MPa；通过二次时效可使合金获得强度1354.9 MPa，电阻率28.8μ?·cm的优异综合性能；合金强化及电学性能提高的主要机制为有序转变。
关键词:
金属材料
,
金基合金
,
电接触材料
,
时效处理
,
有序转变