本文用海洋平台结构钢A537CL1的单边裂纹样品,在空气和3.5％ NaCl水溶液中进行了腐蚀疲劳短裂纹扩展实验,比较不同裂纹长度及环境介质对疲劳短裂纹扩展行为的影响。结果表明,在门槛值附近,对于相同的应力强度因子范围,短裂纹扩展速率比长裂纹扩展快。短裂纹扩展的门槛值随裂纹长度的减小而减小。与空气介质相比较,盐水对疲劳短裂纹扩展加速的程度远大于长裂纹。
关键词:
疲劳短裂纹
,
offshore platform steel
,
environment medium
,
threshold stress intensity
WANG Zhengfu KE Wei Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
ChinaZHU Zuming Insitute of Metal Research.Academia Sinica
,
Shenyang
,
China WANG Zhengfu Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
Acoustic emisssion(AE)behavior during fatigue in either airer or 3.5% NaCl solution has been studied for a structural steel(SM5OB-Zc)as quenched and normalized states.The ex- perimental results show that AE activity is strongly affected by the heat treatment and the condition of environment.Some material constants about A E related with fatigue behavior were obtained and the AE sources in corrosion fatigue were discussed.
关键词:
fatigue
,
null
,
null
,
null
PEI Hongxun YANG Jingjun KE Wei Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
China PEI Hongxun Institute of Corrosion and Protection of Metals
,
Academia Sinica
,
Shenyang
,
China
金属学报(英文版)
The effects of environmental media,both in atmosphere and in 3.5% NaCl aqueous solution, on the growth of short cracks in comparison with the long ones have been investigated under fatigue loading on the specimens of single-edge crack about 0.05—0.15 mm for A537CLI steel.The growth rate of short cracks is faster than those of long ones around the threshoht stress intensity.The threshold stress intensity for short crack growth decreases with de- creasing crack length.The acceleration effect of the salt water,as compared with atmosphere environment,on the growth of short cracks under fatigue is much greater than that on the growth of long cracks.
关键词:
short fatigue crack
,
null
,
null
,
null
周砚磊
,
狄国标
,
刘振宇
,
王国栋
材料热处理学报
对γ＋α两相区淬火后的试验钢板进行300～600℃的回火处理,研究了回火温度对F500级海洋平台用钢组织及性能的影响。结果表明,400℃×1 h回火试样拉伸过程中出现屈服平台,并且回火温度越高不连续屈服现象越明显;回火中,马氏体板条束合并长大,部分位错发生静态回复,密度降低,多边形铁素体含量增加,基体上有大量20～40 nm富Nb的（Nb,Ti）C析出;500～550℃回火可以获得优良的强韧性能,达到F500级别海洋平台钢的要求。
关键词:
海洋平台用钢
,
回火温度
,
析出物
,
冲击韧性
华浩
,
陈蓉
,
李树健
,
赵良
机械工程材料
doi:10.11973/jxgccl201604004
优化了海洋平台用D36钢的化学成分,设计了三种轧制工艺以及两种轧后热处理工艺,研究了不同轧制态和热处理态下该钢的显微组织和力学性能并确定了最佳的轧制工艺及后续热处理工艺,从而实现了生产工艺的优化.结果表明:该钢的优化成分
为0.11~0.12C,0.30~0.40Si,1.55~1.60Mn,≤0.020P,0.005S,0.03~0.06Al,0.045~0.048Nb,0.012~0.018Ti,0.13~0.20Cu,
0.18~0.25Ni,0.055~0.060V,优化轧制及后续热处理工艺为控轧+加速控制冷却轧制后,进行890℃×140 min正火(快速冷却至返红温度650℃)热处理;该工艺下生产的60 mm厚D36钢表面组织以铁素体+马氏体+贝氏体为主,心部组织以细小的铁素体+珠光体为主;其屈服强度为375 MPa,抗拉强度为530 MPa,-20℃冲击功为200 J左右.
关键词:
海洋平台用钢
,
控制轧制
,
正火
,
快冷
,
力学性能
蒋金星
,
唐荻
,
武会宾
,
张杰
,
杨柳
材料工程
doi:10.3969/j.issn.1001-4381.2013.06.007
利用光学显微镜和背散射电子衍射技术对E550海洋平台用钢二次裂纹扩展机理进行了研究,同时对二次裂纹周边的晶粒取向进行了分析.结果表明:钢中的二次裂纹扩展方式与相邻晶粒滑移面的夹角密切相关,其中40％左右的小角度夹角对裂纹扩展影响较小,另外40％左右的相邻晶粒滑移面的夹角为50～62°的大角度夹角,此类夹角的相邻晶粒会在晶界处导致裂纹偏转或起到止裂效果.
关键词:
海洋平台用钢
,
二次裂纹
,
EBSD
狄国标
,
周砚磊
,
麻庆申
,
姜中行
,
刘振宇
钢铁研究学报
研究了空冷条件下，海洋平台用钢中的不同镍含量（WN=0．2％，0．53％，0．8％、1．11％）对其显微组织及力学性能的影响。结果表明，当镍含量较低时，所得显微组织为铁素体和马氏体，晶粒尺寸粗大；随着镍含量的增加，多边形铁素体量降低，针状铁素体量提高，M／A岛更加细小弥散，析出相由相间析出向均匀弥散析出转变，析出粒子尺寸降低；试验钢的屈服强度和抗拉强度随镍含量增加而单调增加，伸长率先增加后降低，而韧脆转变温度先降低后增加，当WN=0．5％～0．83％时，试验钢具有最佳的低温韧性。
关键词:
海洋平台钢
,
析出
,
M/A岛