Y.Z. Zhang(Shanghai Iron and Steel Research Institute
,
Shanghai 200940
,
China)
金属学报(英文版)
The synthetical soft magnetic properties are reported for newly-developed nanocrystalline Fe73.5 Cu1 Nb0.9Mo2.1 Si13.5 B9 and Fe73.5 Cu1 Nb0.5Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3,P2/200k=880 and 973 kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c.4.The dependences of core loss on frequency and amplitude flux density have been analysed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2 kW are reported.
关键词:
nanocrystalline alloy
,
null
,
null
,
null
TONG Huayu
,
DING Bingzhe
,
JIANG Honggang
,
LI Shuling
,
LI Gusong
,
WANG Jingtang State Key Laboratory of RSA
,
Institute of Metal Research.Academia Sinica.Shenyang
,
China
金属学报(英文版)
A new method was developed for preparing nanocrystalline alloy made of the identi- cal compositional Fe_(78)B_(13)Si_9 amorphous ribbon by suitable isothermal annealing.Its microstructure and some structure-sensitive properties.including thermal expansion,spe- cific heat,etc.,have been studied and measured.Comparative analysis of properties was also carried out with amorphous and coarse-grained crystalline alloys of same composi- tion,thus.it is believed that so novel differences in properties from usual materials would be made by the particular microstructure of short range disorder of the nanocrystalline alloy.
关键词:
nanocrystalline alloy
,
null
,
null
,
null
,
null
Y.J.Zhang
金属学报(英文版)
The correlation between the effective magnetic anisotropy ＜k＞ and the temperature T,＜k＞-T curve,for the Fes3Nb6B11 alloys as-cast and annealed at 460 580C was in-vestigated.The experimental results of the ＜k＞-T curves for nanocrystalline sampleswere explained using the theory of exchange interaction between α-Fe grains.
关键词:
nanocrystalline alloy
,
null
,
null
李广敏
,
卢志超
,
李德仁
,
倪晓俊
,
李准
,
冯硕
功能材料
采用SEM和XRD等手段分析了Fe82Cu1B12Si4 Nb1与Fe73.5 Cu1 B7 Si15.5 Nb3纳米晶合金带材在空气中灼烧后的晶化产物和氧化产物;通过降低Nb和Si元素含量,提高Fe和B元素的含量,虽然使Fe82Cu1 B12 Si4 Nb1纳米晶合金具有高饱和磁感应强度和低的矫顽力,但却降低了它的非晶形成和抗氧化能力。根据K.Hono等采用原子探针法观察到的在晶化过程中各元素分布情况,提出了一个晶化过程模型,通过模型分析了纳米晶合金的抗氧化能力的原因;随着晶化过程推进,残余非晶相中Nb元素含量增加,使得残余非晶相区的晶化温度提高,同时发挥限制晶体长大的作用。
关键词:
非晶和微晶金属材料学科
,
纳米晶合金
,
晶化温度
,
抗氧化性
李玳
,
周世同
,
李鹏
,
吕潍威
,
陶静梅
,
朱心昆
材料开发与应用
在纳米结构的金属及合金中,随着晶粒尺寸的下降,晶界体积分数显著增加,使得晶粒长大的驱动力提高,因此纳米金属在加热时(甚至是室温下)是不稳定的,限制了其加工与应用.本文对Trelewicz/Schuh (TS)模型进行了修正,并利用修正的模型对Cu-6.5at％ Zr、Cu-6.5at％ Nb纳米晶合金的热力学稳定倾向进行了计算研究.实验利用机械合金化的方法制备这两种纳米晶合金,并在不同温度下进行退火.实验结果及理论计算表明,随着溶质原子的加入及在晶界的偏聚,这两种纳米晶合金的晶粒长大得到抑制,热力学稳定性提高.
关键词:
纳米晶合金
,
机械合金化
,
热力学稳定
,
晶界偏聚
甘章华
,
周欢华
,
戴义
,
刘静
材料科学与工程学报
采用单辊甩带机在大气环境下制备了一种低硼含量的Fe75.5Si13.5bB7Cu1Nb1.5V1.5合金 薄带.该合金薄带的XRD图谱呈现一个宽峰,表明薄带具有非晶态结构.与Fe73.5Si13.5B9Cu1Nb3非晶合金原带相比,Fe75.5Si13.5B7Cu1Nb1.5V1.5非晶合金原带的韧性大幅提高,可对折一次不断.经过优化530℃×60min晶化退火后,发现随频率增高,该合金的相对磁导率下降趋势缓慢,高频下的相对磁导率优于Fe73.5Si13.5B9Cu1Nb3纳米晶合金.
关键词:
纳米晶合金
,
高韧性
,
相对磁导率
,
高频
佟华宇
,
丁炳哲
,
姜洪刚
,
李淑苓
,
李谷松
,
王景唐
金属学报
采用适当的热处理工艺将相同成分的Fe_(78)B_(13)Si_9非晶态合金条带晶化制备成纳米晶合金;测定并研究了纳米晶合金的微观结构(晶体结构及尺寸)和一些结构敏感性能(热膨胀、比热),同时,将其与同样成分的非晶态、大晶粒状态合金的性能进行比较分析,认为由于纳米晶合金特殊的微观结构(短程无序),使其在性能上表现出与通常材料有很大差异。
关键词:
纳米晶合金
,
Fe_(78)B_(13)Si_9
,
microstructure
,
thermal expansion