Ni_(100-x)Mo_x(x=20,30,38)alloys have been synthesized by mechanical alloying.The structure evolution of powders in mechanical alloying process has been monitored by X-ray diffraction,scanning electron microscopy and transmission electron microscopy analyses.The results show that the Ni_(62)Mo_(38)sample becomes partially amorphous after high energy ball milling,while the Ni_(80)Mo_(20)and Ni_(70)Mo_(30)become non-equilibrium nanocrystals.
关键词:
mechanical alloying
,
null
,
null
,
null
吴莹
,
闻荻江
,
徐玲
,
王振平
材料科学与工程学报
doi:10.3969/j.issn.1673-2812.2006.01.007
以3,3',5,5'-四甲基联苯胺(TMB)与Keggin结构钼磷酸H3PMo12O40杂化,合成得到新型分子杂化材料,经元素分析及IR、ICP、XRD等手段表征,确定其分子结构为(TMB)3PMo12O40,TEM显示该分子杂化材料颗粒直径在40nm～60nm,分布均匀,属球形颗粒纳米晶,UV-vis和ESR谱证明(TMB)3PMo12O40分子杂化材料为电荷转移型超分子化合物,并具有显著的光敏性和电催化活性.
关键词:
纳米晶
,
分子杂化材料
,
电荷转移
,
钼磷酸
,
3,3',5,5'-四甲基联苯胺
李东卫
,
林健
,
雷淑华
,
卞亓
,
覃爽
功能材料与器件学报
doi:10.3969/j.issn.1007-4252.2009.05.001
利用直流电场诱导热扩散技术,引导金属银离子扩散进入硅酸盐玻璃基片内部,并通过后续热处理析出金属银纳米晶体.研究发现,随着电场强度的增大和扩散温度的升高,扩散进入到玻璃基片中的金属银离子数量也随之增多.电场诱导热扩散后银以Ag~+和Ag~0的形式存在于玻璃基片中.经后续热处理在玻璃基片中形成2～5nm的金属银纳米晶粒,并在410 nm附近产生明显的表面等离子共振吸收现象;银纳米晶体主要分布在基片表面以下30～100μm区域.
关键词:
硅酸盐玻璃
,
直流电场
,
纳米晶
,
扩散
涂国超
,
张家骥
,
季雨
,
史长利
金属学报
本文研究了nm级微晶软磁材料Fe-Cu-Mo-Si-B合金系在不同磁退火方式以及不同热处理温度下磁性能的变化。结果表明,最佳热处理为510℃,保温1h;以缓慢冷却性能最好,并利用透射电镜,X射线衍射及热磁曲线对最佳热处理状态下的样品进行了组织观察和结构确定。该材料由两相组成:一相是a-FeSi固溶体,尺寸在10—20nm之间;另一相为非晶态。
关键词:
纳米微晶
,
soft magnetic material
,
Fe-base alloy