ALPHA-PHASE MICROCRYSTALLINE STRUCTURE OF IONITRIDING LAYER ON STEELS

LI Ji YUAN Yongsheng Northeast University of Technology , Shenyang , ChinaYUAN Keqi University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

TEM observation on the ionitriding layer was carried out on steels W18Cr4V,38CrMoAl and 1Cr18Ni9Ti,and AES of elementary analysis was also made on the outer surface of ionitrid- ing layer of austenitic stainless steel.Perhaps due to the ion-bombardment effect,a microcrystalline structure with texture was affirmed along surface of the ionitriding layer.It may be affected by cathodic sputtering and absorption that the atomic ratio of Cr/Fe in- creases and of Ni/Fe decreases on surface of nitriding layer on austenitic stainless steel 1Cr18Ni9Ti,thus the α-phase microcrystalline structure occurrs.

关键词: ionitriding , null , null

钢的离子氮化表层中的α相微晶结构

李冀 , 苑永生 , 苑珂琦

金属学报

对W18Cr4V,38CrMoAl,1Cr18Ni9Ti3钢种的离子氮化层进行了透射电镜观察,并对奥氏体不锈钢的离子氮化表层用Auger能谱进行了成分分析,由于离子轰击效应,在离子氮化表层形成了α相微晶结构,其中存在织构.在离子轰击渗扩过程中,1Cr18Ni9Ti奥氏体不锈钢的渗层的表层发生成分变化,Cr/Fe比升高,Ni/Fe比下降,所以也形成了α相微晶结构。

关键词: 离子氮化 , microcrystal , surface structure

H13钢离子氮化前后表面沉积CrAlN薄膜的耐氯离子腐蚀性能

彭彦彬 , 余春燕 , 王社斌 , 韩培德 , 李天宝

机械工程材料

在离子氮化前后的H13钢表面沉积了CrAlN薄膜,研究了其在质量分数为3.5%的NaCl溶液中的耐腐蚀性,并用场发射扫描电镜观察了薄膜腐蚀前后的表面形貌。结果表明:H13钢基体表面沉积CrAlN薄膜后的耐腐蚀性能显著提高;经离子氮化和表面沉积CrAlN薄膜复合处理后,耐腐蚀性进一步提高,试验后表面没有出现明显的腐蚀坑及膜层脱落。

关键词: CrAlN薄膜 , 耐腐蚀性 , 离子氮化