杨长林
,
杨根仓
,
刘峰
,
周尧和
金属学报
通过真空熔炼和气体保护, 采用熔融玻璃与循环过热相结合的深过冷快速凝固技术,研究了影响富Fe端Fe-B共晶合金熔体净化效果的主要因素, 确定了该合金熔体获得超过冷的净化方法, 并使Fe83B17共晶合金熔体稳定获得了300-460 K的超过冷度, 使Fe80B20过共晶合 金熔体的过冷度达到了485 K, 从而使Fe-B共晶系合金熔体开始形核前的初始过冷度达到了0.3m-0.4m的水平. 通过对冷却曲线的分析, 讨论了表征超过冷快速凝固的热力学特征.
关键词:
玻璃净化
,
hypercooling
,
undercooling
,
Fe-B eutectic alloy
G.S. Song
,
Z.Z. Zhang
,
X.B. Dong
,
G.C. Yang and Y.H. Zhou(State Key Laboratory of Solidification Processing
,
Northwestern Polytechnical University
,
Xi'an 710072
,
China)
金属学报(英文版)
Undereooling eoperiments on binary Ni50 Cu50 alloy melts were conducted. The hypercooling limit of this alloy, which is about 310K, was evaluated by mcasuring plateau time needed for the interkendritic liquid solidification and extmpolating this function to zero. This limit was exceeded first in the binary alloy undereooled by about 320K.The effect of liquid undercooling on the respective microstructure evolution was studied by optical metallogrnphy. The hypercooled microstructure contains rcsidual fragments within grain boundaries and is quite different from those obtained at undercoolings below 310K. The finding indicated the existence of dendrite break up. The dendrite break up may be induced either by remelting or by stress. By considering hyperrooling conditions and comparing two grain ndnement microstructures observed at small and larpe undereoolings, the forms of dendrite break up and the grain refinement mechanism exceeding the hypereooling limit are further discussed.
关键词:
hypercooling
,
null
,
null
,
null