The hot deformation characteristics of GH4720Li alloy were studied at the temperature of 1100-1170 ℃ and strain rate of 001-1 s-1 using Gleeble hot compression tests. True stress-true strain curves and deformation microstructures were investigated. Constitutive equation was established using the hyperbolic law. Processing map for hot working was also developed on the basis of the variations of efficiency of power dissipation with temperature and strain rate. The results show that dynamic recrystallization is the dominant softening mechanism during hot deformation. Fully recrystallized grain is obtained at strain of 07 above 1130 ℃, and coarsening occurs above 1150 ℃. The mean deformation activation energy is determined to be 512 kJ/mol. According to the low activation energy value, high dissipation efficiency parameter and fine recrystallized microstructure, 1130 ℃ is chosen as the hot working temperature for GH4720Li alloy.
关键词:
hot deformation
,
GH4720Li alloy
,
constitutive equation
,
processing map
CAO Jin-rong
,
LIU Zheng-dong
,
CHENG Shi-chang
,
YANG Gang
,
XIE Jian-xin
钢铁研究学报(英文版)
Based on dislocation reaction theory and Avrami equation, a constitutive equation model was developed to describe dynamic recovery and dynamic recrystallization during hot deformation of T122 heat resistant steel, which have taken the effect of dynamic strain aging into account. Uniaxial hot compression test had been carried out over a wide range of strain rate (001 to 10 s-1) and temperature (900 to 1200 ℃) with the help of Gleeble 3500. Obtained experimental data was applied to determine the material parameters in proposed constitutive equations of T122 steel, by using the non-linear least square regress optimization method. The calculated constitutive equations are quantitatively in good agreement with experimentally measured curves and microstructure observation. It shows that propose constitutive equation T122 steel is able to be used to predict flow stress of T122 steel during hot deformation in austenite temperature scope.
关键词:
hot deformation
,
dislocation
,
constitutive equation
,
T122 heat resistant steel
文新理
,
蒋波
,
晁智勇
,
李海滨
,
刘雅政
,
周乐育
材料热处理学报
在Gleeble-1500热模拟试验机上对低Mo管线钢X80进行了不同热变形条件下的压缩试验,分析了变形温度、变形量和变形速率对材料组织特征和相变动力学的影响,结果表明:随变形温度的降低,低Mo管线钢X80奥氏体(γ)晶界变得不明显,板条贝氏体(LB)变短且数量减少,变形温度对相变动力学的影响不大;随变形量的增加,板条贝氏体和粒状贝氏体(GB)减少而针状铁素体(AF)增多,板条贝氏体束(Bainite Packet)内的M/A岛尺寸减小且分布更加弥散化,相变动力学曲线右移;随变形速率的降低,奥氏体晶界的多边形特征变得不明显,板条贝氏体数量减少,M/A岛尺寸减小且分布弥散化,相变动力学曲线右移.
关键词:
热变形
,
低Mo管线钢X80
,
显微组织
,
相变动力学