A large undercooling level up to 550k (0.386TE) was achieved in eutectic Ni78.6Si21.4 melt by the combination of molten-glass and cyclic superheating. A microcrystalline structure is obtained at large undercooling. Surprisingly, the morphology of a(Ni) phase transits from the non-faceted phase to faceted phase at large undercooling of 390K . Based on the classical nucleation theory and transient nucleation theory, the process of microstructure evolution and competitive nucleation was analyzed, and the refinement of crystal structure is determined by the high nucleation rate under large undercooling.
关键词:
high undercooling
,
融融玻璃
,
共晶
,
快速凝固
刘宁
,
杨根仓
,
刘峰
,
陈豫增
,
杨长林
,
周尧和
金属学报
采用熔融玻璃净化法研究了深过冷Fe-Co合金的凝固组织演化规律. 随着熔体过冷度的增加，除Fe90Co10合金外，Fe100－x-Cox(x=10－40)合金凝固组织都经历了两次晶粒细化过程; 而当过冷度大于某一临界过冷度时，凝固组织不再是单相，而是出现了亚稳相组织。研究结果表明，除了小过冷度下的组织转变以外，凝固组织转变过冷度以及亚稳相形成的临界过冷度随着Co含量的增加而增大。此外，本文运用BCT模型和瞬态形核理论对凝固组织的演化规律进行了理论分析。
关键词:
Fe-Co合金
,
solidification
,
high undercooling
严军辉
,
坚增运
,
朱满
,
常芳娥
,
许军锋
金属学报
doi:10.11900/0412.1961.2015.00553
通过电磁悬浮(EML)熔炼设备对Al-70%Si合金进行深过冷处理, 利用高速摄影仪(HSC)和SEM分别对凝固过程和凝固后的组织进行了观测, 研究了不同过冷度下初生Si的生长规律. 结果表明, 过冷度对初生Si的生长有很大影响. 当过冷度较小时, 初生Si为粗大的长条状, 有特殊的边和面, 且具有明显的孪晶痕迹, 表现出小平面生长的特征; 当过冷度较大时, 初生Si为细小的枝晶和球状晶, 表面光滑, 表现出非小平面生长的特征; 当过冷度居于中间时, 初生Si为粗大的块状和规则排列的枝晶状, 块状有特殊的边和面, 枝晶表面光滑, 表现出小平面和非小平面混合生长的特征. 随着过冷度的增加, 初生Si的生长方式由小平面生长转变为中间方式生长, 再由中间方式生长转变为非小平面生长, 生长方式间发生转变的临界过冷度分别为122 和230 K.
关键词:
Al-70%Si合金
,
电磁悬浮
,
高速摄影仪
,
深过冷
,
初生Si
,
生长方式
严军辉
,
坚增运
,
朱满
,
常芳娥
,
许军锋
金属学报
doi:10.11900/0412.1961.2015.00553
通过电磁悬浮(EML)熔炼设备对Al-70％Si合金进行深过冷处理,利用高速摄影仪(HSC)和SEM分别对凝固过程和凝固后的组织进行了观测,研究了不同过冷度下初生Si的生长规律.结果表明,过冷度对初生Si的生长有很大影响.当过冷度较小时,初生Si为粗大的长条状,有特殊的边和面,且具有明显的孪晶痕迹,表现出小平面生长的特征;当过冷度较大时,初生Si为细小的枝晶和球状晶,表面光滑,表现出非小平面生长的特征;当过冷度居于中间时,初生Si为粗大的块状和规则排列的枝晶状,块状有特殊的边和面,枝晶表面光滑,表现出小平面和非小平面混合生长的特征.随着过冷度的增加,初生Si的生长方式由小平面生长转变为中间方式生长,再由中间方式生长转变为非小平面生长,生长方式间发生转变的临界过冷度分别为122和230 K.
关键词:
Al-70％Si合金
,
电磁悬浮
,
高速摄影仪
,
深过冷
,
初生Si
,
生长方式