金属学报
用Auger谱仪、电子探针分析和透射电镜、扫描电镜观察等手段,考察了高温复压处理对93钨合金磷偏析的影响。发现在1200—1500℃保温后炉冷,在钨-钨晶界特别是钨-粘结相相界上存在磷偏析,而在该温度范围复压后炉冷,则未发现磷在晶界和相界上偏析;复压处理态材料粘结相中位错直接影响磷向界面偏析,为退火处理的材料因磷在界面偏析而引起机械性能下降。
关键词:
钨合金
,
high temperature repressing
,
interface
,
P segregation
,
dislocation
LI Zhi XI Jukui YANG Yunlin Luoyang Institute of Technology
,
Luoyang
,
China
金属学报(英文版)
The influence of high temperature repressing treatment on the segregation of phosphorus in the 93W alloy was carefully investigated by means of Auger electron spectroscope,EPMA, TEM and SEM.The segregation of phosphorus has been observed at the tungsten-tungsten grain boundaries,particularly at the tungsten-matrix interphases when the specimens were kept at the temperature in the range of 1200—1500℃ ,followed by furnace cooling.However, no segregation of phosphorus was observed at the interfaces after the specimens were re- pressed at the range of temperature,followed by furnace cooling.After investigation,the dis- locations in the matrix phase of as-repressed specimens directly influenced the phosphorus segregation to the interfaces.After annealing,the mechanical properties were reduced because of the phosphorus segregation at the interface boundaries.
关键词:
93W-4.5Ni-2.5Fe alloy
,
null
,
null
,
null
,
null