METHOD FOR POLYFAMILY PLANE TRACE ANALYSIS AND ITS APPLICATION

LI Yuqing Research Institute of Daye Steel Works , Huangshi , China Senior Engineer , Research Institute of Daye Steel Works , Huangshi 435001 , China

金属学报(英文版)

The formula for calculating included angle between polufamily plane traces of lattice systems in thin foit under hath zero tilt and non-zero tilt states was deduced and verified by certain prat tical examples.The method may be available to index the plane traces of slip.twin and other defects.especially to determine such planar defects as twin and other defects esperially

关键词: polyfamily plane , null , null , null

工业纯铝在室温和深冷轧制条件下的微尺寸效应

汤德林 , 刘相华 , 宋孟

材料热处理学报

对1060工业纯铝分别进行室温轧制和深冷轧制,取成品厚度为300、200、100、50和25 μm 5组试样进行拉伸试验.结果表明,经过室温轧制的轧件,当其厚度减薄至100 μm时出现微尺寸效应,即厚度大于100 μm时随厚度减小抗拉强度增大,厚度小于100 μm时随厚度减小抗拉强度减小;发现100 μm是纯铝室温轧制时出现尺寸效应的临界值.与室温轧制相比,经过深冷轧制轧件微尺寸效应的临界值相同而表现形式不同,厚度小于临界值100 μm后其抗拉强度随厚度减小而增加的速度加快.在相同厚度条件下,深冷轧制后的轧件比室温轧制的晶粒内部亚结构更细小,分析认为这是其强度高于室温轧制的一个原因.

关键词: 极薄带 , 深冷轧制 , 抗拉强度 , 微尺寸效应