材料科学技术（英文）
A comprehensive review of low temperature environmental embrittlement in intermetallics is pres- ented. Moisture and hydrogen are shown to severely embrittle many intermetallics, including iron, nickel and titanium aluminides. The roles of composition, microstructure and external test variables are emphasized. Several methods to reduce or avoid embrittlement are described.
关键词:
environmental embrittlement
,
null
,
null
彭真
,
王振生
,
苏新
,
郭建亭
,
周兰章
,
汪梅
稀有金属
doi:10.13373/j.cnki.cjrm.XY15101501
采用电弧离子镀(AIP)技术在K417G合金表面制备了NiCrAlYSi涂层,利用HRS-2M型往复磨损试验机测试了K417G合金及NiCrAlYSi涂层室温至400℃以下的摩擦磨损特性,利用扫描电镜(SEM),能谱分析(EDS)和X射线衍射(XRD)等手段对合金和涂层的磨损表面形貌和横截面形貌进行观察和分析.结果表明:K417G合金的磨损率低于NiCrAlYSi涂层,300℃以下,合金摩擦系数高于涂层.室温下,合金和涂层磨损机制是疲劳脱层和环境致脆,环境致脆磨损机制源于室温空气中Ni3Al相的环境脆性;磨损过程中,磨损表面形成的新鲜表面中的Ni3Al相中的Al+与水汽反应生成原子态H且逐渐聚集,导致氢致环境脆性,并逐渐作用于磨损表面;磨损表面的裂纹源在γ/γ'界面处形核,裂纹既沿着γ/γ'界面扩展,又进入γ'晶粒,呈现沿晶和穿晶混合状.随磨损温度升高,Ni3Al相的环境脆性消失,合金和涂层磨损表面的环境致脆特征消失,磨损机制转变为黏着、犁沟、块状剥落和氧化磨损机制.
关键词:
K417G合金
,
NiCrAlYSi涂层
,
环境脆性
,
疲劳脱层
,
摩擦磨损性能
王振生
,
彭真
,
杨双双
,
郭建亭
,
周兰章
,
谭清奇
,
苏新
中国有色金属学报
研究K417G合金及其表面Ni(Co)CrAlYSi涂层在室温大气环境下的磨损特性。结果表明：K417G合金及其表面Ni(Co)CrAlYSi涂层的磨损受磨损亚表层疲劳脱层和磨损表面环境脆性的共同作用，致使其磨损率高于纯Ni的。在磨损过程中，环境脆性逐渐作用于磨损表面，磨损表面的裂纹源在γ/γ′界面以及碳化物与合金基体界面形核，裂纹既沿着γ/γ′面以及碳化物与合金基体界面扩展，又进入γ′晶粒，呈现沿晶和穿晶混合状。
关键词:
K417G合金
,
Ni(Co)CrAlYSi涂层
,
Ni 3 Al
,
摩擦
,
磨损
,
环境致脆