Supawan Vichaphund Duangduen Atong
材料科学技术（英文）
This work reports two preparation methods of Ni-Al2O3 composite to be used as a hydrogen separation membrane. The first method was powder impregnation while the second method was soaking-drying-firing or bulk impregnation. In the first method, the 10 wt pct Nickel (II) nitrate hexahydrate solution was mixed with Al2O3 powder. The mixed powders were dried at 100°C and uniaxially pressed into a disk shape at 7 MPa. The densification of composite membranes was accomplished by pressureless sintered at 900-1300°C. For the second preparation method, the Al2O3 disk support was prepared firstly by uniaxially pressing Al2O3 powder at 7 MPa and then sintered at 1000-1200°C for 2 h. After that, the Al2O3 support was soaked into 10 wt pct Ni solution, dried at 100°C and calcined at 900°C for 2 h. The soaking-drying-firing sequence was repeated ten times to finally obtain the Ni-Al2O3 membranes. After preparation process, the membranes fabricated from these two methods were reduced at 910°C for 2 h in hydrogen atmosphere. The effect of the preparation method on properties of membranes in terms of density, porosity, phase and microstructure are discussed.
关键词:
Composite membrane
,
hydrogen separation
,
Nickel
,
Alumina
曾高峰
,
史蕾
,
徐恒泳
催化学报
研究了不同Pd~(2+)含量的镀液在多孔陶瓷载体上的化学沉积规律,发现当Pd沉积层厚度达到约5μm后,即使镀液中反应物的消耗比例很小,膜厚增长也明显变缓,沉积反应主要受膜层表面的催化活性位控制;当镀液中Pd~(2+)含量只能沉积形成小于4μm的Pd膜时,在323K化学镀180min后,镀液中Pd~(2+)的转化率高于90%.与之相似,当Ag镀液中的Ag~+含量等于0.5～2μm的Ag膜层所需量时,在333K化学镀120min后,Ag~+的转化率可达95%.Ag~+的高转化率与Ag颗粒的择向生长特性有关.根据Pd和Ag的化学镀沉积规律,通过调节镀液中金属离子的含量能够预先设计和精确控制超薄Pd/Ag膜的膜厚和组成.
关键词:
钯
,
银
,
复合膜
,
化学镀
,
膜厚控制
,
组成控制
,
沉积规律
叶佳梅
,
崔夏雯
,
钱伟
,
杨文盼
,
王志峰
,
刘俊亮
,
张明
高分子材料科学与工程
为开发具有长效抗菌高分子材料以满足人们对其日益增长的需求，以天然提取物茶多酚为抗菌剂，壳聚糖为改性剂，尼龙6为基体，通过溶液涂膜成功制备了高分子复合抗菌薄膜，并讨论了抗菌剂含量、基体组成等对复合薄膜亚微观结构及抗茵性能的影响。结果表明，未加壳聚糖时，抗菌复合薄膜中，茶多酚多以吸附形式存在于尼龙6球形线团表面，其降低了尼龙6高分子链之间的相互作用力与链排列规整性；当加入壳聚糖时，所得抗菌复合薄膜的基体转变成为丝状、层状结构，同时，壳聚糖的存在有效地保护了茶多酚，使其复合薄膜抗菌性能显著地提高。
关键词:
茶多酚
,
复合薄膜
,
微结构
,
抗菌性能
马诚
,
孔瑛
,
杨金荣
,
杨威
,
韩晓磊
高分子材料科学与工程
以乙基纤维素（EC）和正钛酸丁酯（TBT）为主要原料,通过溶胶-凝胶（Sol-Gel）法制备了EC/TiO2复合膜。研究了TiO2粒子在复合膜中分布形貌、复合膜的结构变化及对气体渗透和分离性能的影响。结果表明,TiO2质量分数达到25%时,微米级的TiO2粒子均匀分散在复合膜中,复合膜形成有机-无机三维网络结构,测试气体在膜中的渗透行为主要受动力学因素控制,其中H2、O2透气系数分别增大至纯EC膜的1.8倍和1.3倍,H2/N2及O2/N2分离性能略有提高。
关键词:
乙基纤维素
,
溶胶-凝胶法
,
复合膜
,
气体分离
王铭
,
赵晓燕
,
刘远
,
纪俊玲
高分子材料科学与工程
以醋酸纤维素(CA)为膜阻隔层,聚羟基丁酸/戊酸酯共聚物(PHBV)作为膜支撑层,利用静电纺丝法制备出复合膜.研究了醋酸纤维素质量分数、溶剂配比、电压,以及CA与PHBV复合比(体积比)对纤维形态及复合膜性能的影响,并通过扫描电镜表征了CA纤维膜的表面形貌.研究结果表明,当CA的质量分数为12％,溶剂丙酮与N,N-二甲基乙酰胺(DMAc)体积比为1/1,纺丝电压为14 kV时,CA纤维膜形态均匀,并呈现独特的双纤维直径交错结构.这种结构的膜材料有利于在提高水通量的同时,保持其较好的截留率.同时,当CA/PHBV的复合比为10/10时,复合膜的水通量能达到104数量级,截留率可以达到87％.
关键词:
静电纺
,
醋酸纤维素
,
聚羟基丁酸/戊酸酯共聚物
,
复合膜
,
纤维
刘琨
,
祖敏辉
膜科学与技术
doi:10.3969/j.issn.1007-8924.2010.01.012
为从醋酸正丁酯稀水溶液中回收微量酯,采用涂布法制备了聚醚共聚乙酰胺/聚偏氟乙烯(PEBA/PVDF)复合膜.考察了复合膜在醋酸正丁酯稀水溶液中的溶胀性能,探讨了浸泡时间、浸泡液温度及浸泡液浓度等因素对溶胀度的影响.通过拉力试验,测试了复合膜的力学性能.通过渗透汽化实验,从醋酸正丁酯稀水溶液中分离出醋酸正丁酯,研究了料液浓度、料液温度等因素对复合膜分离性能的影响.结果显示,复合膜在醋酸正丁酯稀水溶液中具有良好的溶胀性能及渗透汽化性能;40℃下分离质量分数为0.6%的醋酸正丁酯水溶液,渗透通量达到280.43 g/(m~2·h),分离因子为308.65.
关键词:
聚醚共聚乙酰胺(PEBA)
,
聚偏氟乙烯(PVDF)
,
复合膜
,
溶胀
,
渗透汽化
王薇
,
孙静
,
王宝春
高分子材料科学与工程
正渗透是新的非热能驱动膜过程。采用界面聚合的方法制备了中空纤维复合膜。以Na2SO4、MgSO4、NaCl和Mg-Cl2水溶液作为驱动液进行了正渗透实验。实验表明,正渗透通量随着驱动液浓度的增加而增加,其中Na2SO4、MgCl2水溶液的渗透通量大于MgSO4、NaCl水溶液的。驱动液中无机盐向原水中扩散的渗透速率随无机盐浓度的增加而增加,且MgCl2〉NaCl〉Na2SO4〉MgSO4。原水流速对正渗透通量的影响极小,而驱动液流速对正渗透通量的影响较大。
关键词:
正渗透
,
复合膜
,
驱动液
,
渗透性能
周伟涛
,
黄海涛
,
何建新
,
崔世忠
材料科学与工程学报
本文以乙醇处理后丝素蛋白(SF)纳米膜为载体,通过逐层自组装方法制备SF-PEI(聚乙烯亚胺)涂层复合纳米纤维膜.通过SEM、FTIR、TG-DTA、XPS分别研究多层SF-PEI复合纤维膜的形貌、结构和性能.结果表明:少于5层SF-PEI涂层纤维膜保持良好的纤维形貌和基本特征,是理想的潜在重金属离子吸附材料.但继续增加自组装层数(6层SF-PEI),纤维表面有明显的粘附物,且纤维彼此间粘连严重,形貌恶化.IR、TG-DTA和XPS分析结果表明,PEI大分子已被吸附于SF表面,形成了多层自组装SF PEI复合纤维膜,且复合膜中N1s以单峰的形式存在,反应了自组装后PEI中“N”元素的价态没有改变,说明自组装涂层纤维膜层与层之间主要是依靠简单的静电相互作用.通过控制自组装的层数,可以得到具有理想结构和性能的复合纳米纤维膜.
关键词:
聚合物电解质
,
多层自组装
,
纳米纤维
,
复合膜
,
表面化学性质
陈志昌
,
陈思浩
,
王继虎
,
徐刚
,
杨春宇
材料导报
doi:10.11896/j.issn.1005-023X.2015.22.008
通过改性Hummers法制备了石墨烯,然后通过物理共混与超声相结合的方法制备了石墨烯含量不同的石墨烯/聚乳酸复合膜,并研究复合膜的电阻、力学性能、热稳定性和气体阻隔性能.其中纯的聚乳酸膜的电阻数量级为1016,而添加0.5％的石墨烯之后,其电阻值数量级可达104,提高了12个数量级;当添加量为1％时,其拉伸强度也从15 MPa增加到20 MPa,透气量也从1650 cm3/(m2·24 h·0.1 MPa)降低到300 cm3/(m2·24 h·0.1MPa);添加量为5％时,热阻值从13.4 cm2·K/W降低到7.2 cm2·K/W.
关键词:
石墨烯
,
聚乳酸
,
复合膜
,
热稳定性
,
气体阻隔性能
施奕磊
,
杨腊文
,
蒋仲庆
,
贾志舰
,
蒋仲杰
膜科学与技术
doi:10.16159/j.cnki.issn1007-8924.2015.05.020
氧化石墨烯(graphene oxide,GO)和磺酸化氧化石墨烯(sulfonated graphene oxide,SGO)是石墨烯的衍生材料,具有两亲性能、超高的比表面积、良好的电子绝缘性和柔韧性,使其作为掺杂材料在燃料电池、电膜分离过程、扩散渗析、电化学分析和传感等领域具有广泛的应用前景.本文主要综述了GO和SGO在质子交换膜(PEM)中的应用.质子交换膜是燃料电池的重要组成部分,在燃料电池中主要起传导质子和防止燃料渗透的作用.当前商用化的燃料电池电解质膜主要存在质子导电性低、燃料渗透率高、稳定性差等问题.GO和SGO的掺入可以提高膜的质子导电性和稳定性、降低膜的燃料渗透率,因此对提高膜的性能以及燃料电池的性能具有十分重要的作用.本文主要概括了近几年来GO及SGO在质子交换膜中的应用研究进展,并系统地介绍了GO及SGO对Nafion及新型的非氟类聚合物质子交换膜材料性能的影响.
关键词:
氧化石墨烯
,
磺酸化氧化石墨烯
,
质子交换膜
,
燃料电池
,
复合膜