Y. T. Xing
,
Y.Z. Wang
,
G.W. Qiao
金属学报(英文版)
The paramagnetic Meissner effect (PME) was observed on the field-cooled M-T curvesof melt-textured Y0.99Nd0.01Ba2Cu3O7-y in applied magnetic fields from 1kOe toJ0kOe. In the magnetic field below 1kOe, the sample undergoes the typical transi-tion from the normal state to the superconducting state when it was cooled down. Theapplied magnetic fields in which the PME occurs, are very high compared with thefields reported in literatures. We propose that the occurrence of the PME may be dueto a phase transition of flux vortices in the superconductors.
关键词:
YBCO superconductor
,
null
石盼盼
,
孙爱民
,
马书懿
,
王丹
,
张明发
低温物理学报
采用固相反应法制作了在不同烧结温度对Sn掺杂下的YBCO一系列样品.本文采用了X-射线衍射仪,电阻测量和SEM对样品物相形成,微观结构,晶格常数以及超导转变温度进行表征,测量结果表明:不同的烧结温度会影响Sn离子的形式,随着温度的升高,Y-123峰明显减弱,杂峰相增多.本文分析了晶格常数与超导性存在必然联系,SEM结果表明第二相粒子的形成以及表面形貌都与温度有关.
关键词:
YBCO超导
,
Sn掺杂
,
微观结构
,
烧结温度(℃)
艾小倩
,
孙爱民
,
赵懂叶
,
鲁彦忠
,
刘恒伟
,
马耀通
,
罗晶
,
贾续旭
,
郭建平
低温物理学报
本文用固相反应法制备了Y1-xCax（Ba1-xCex）2Cu3O7-δ（x=0～0．1）一系列样品．利用X射线衍射法（XRD）对其粉体的物相进行了表征，发现随着掺杂量的增加，样品的晶体结构有从正交相向四方相转变的趋势．采用标准四端引线法系统的测量了样品的超导电性，发现随着掺杂量的增加，样品的超导转变温度呈逐渐降低的趋势．并对实验结果进行了详细的理论分析．
关键词:
YBCO超导体
,
固相反应法
,
超导转变温度