The TEM and HRTEM were utilized to investigate the phase transformation of hydrogenated Ti-6Al-4V alloys (0 wtpct-0.9 wt pct H) treated by annealing and quenching from β field. The results indicate that the orthorhombic α'' martensite and β phase appear progressively with the increase of hydrogen concentration. On the other hand, hydrides with sizes of 2-5 nm are observed in the specimens containing more than 0.6 wt pct hydrogen. The formation of α'' and twins can be attributed to the internal stress caused by solid solution of hydrogen and hydrides precipitation.
关键词:
Ti-6Al-4V alloys
,
Martensitic transformation
,
Hydrogenation
,
Hydride
张云鹏
,
周泽宇
,
闫妍
材料开发与应用
采用分离式Hopkinson压杆(SHPB)加载装置,分别用200 mm和150 mm打击杆以28 m/s速度对Ti-6Al-4V合金帽形试样进行强迫剪切实验,利用OM、SEM、TEM等手段分析了强迫剪切条件下Ti-6Al-4V合金的绝热剪切带演化特征和高应变率剪切变形条件下的失效模式.结果表明,在本文所述实验条件下,Ti-6Al-4V合金的绝热剪切带(ASB)表现为“白亮带”;ASB的宽度随加载时间的延长而增加;ASB边缘的裂纹是由于ASB的变形与基体的不协调而产生的,ASB中心部位的裂纹是由于非晶形成而后破碎导致的.
关键词:
Ti-6Al-4V合金
,
绝热剪切带(ASB)
,
强迫剪切