The sintering additives such as Al2O3 and/or Y2O3 were coated on the surfaces of Si3N4 particles via heterogeneous nucleation processing using a buffered pH solution as the precipitation reagent. They nucleated and grew only on the surfaces of Si3N4 and did not form sol particles in solution by TEM observation. The isoelectric point (IEP) of coated Si3N4 was different from that of as-received Si3N4. The IEP of Al(OH)3-coated Si3N4 occurred at pH8.4, which is close to that of alumina. When Al(OH)3-coated Si3N4 particles were coated with Y(OH)3, the IEP of coated Si3N4 powder shifted from pH8.4 to pH9.2, similar to that of yttria. In addition, the rheological data showed that Al2O3 and/or Y2O3 coated Si3N4 suspension is nearly Newtonian and that added Si3N4 suspension shows a shear rate thinning behavior.
关键词:
Si3N4 powder
,
null
,
null
,
null
代建清
,
黄勇
无机材料学报
doi:10.3724/SP.J.1077.2008.00165
选用四种商业氮化硅粉料(其中FD1、FD2和M11均由硅粉直接氮化法合成但后处理工艺不同, 而UBE粉的合成采用亚胺基硅热分解法), 系统研究了酸洗和热氧化处理对其表面特性和水基浆料流变特性的影响. 研究表明, 表面基团的种类和数量、可溶性高价反离子浓度以及离子电导率是影响氮化硅粉料在水中分散性能的关键因素. FD1粉料分散性能差的原因是可溶性高价反离子浓度太高, FD2粉料分散性能差的关键是颗粒表面存在Si-O-C-R憎水基团, M11粉料分散性能不好源于离子电导率过大, 而UBE粉料表面的大量Si-O-Si基团是其分散性能差的限制性因素. 经表面改性处理的四种氮化硅水基浆料具有良好的流变特性.
关键词:
氮化硅粉料
,
dispersibility
,
acid-leaching
,
thermal oxidation