Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the joint were measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the Si3N4/ Si3N4 joints were obtained by brazing at 1373～1473 K for 0.9～5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on the shear strength of the joint was investigated. When the brazing temperature and holding time is 1423 K and 5.4 ks respectively, the maximum shear strength of the Si3N4/Si3N4 joint is obtained to be 198 MPa.
关键词:
Si3N4 ceramic
,
null
,
null
,
null
唐修检
,
王健全
,
田欣利
,
刘谦
,
吴志远
,
雷蕾
人工晶体学报
建立了氮化硅陶瓷的准静态单晶压痕崩碎损伤实验系统,应用声发射三维定位系统实时监测其损伤演化过程,应用三维显微系统观测陶瓷崩口损伤表面形貌,并分析了崩碎损伤过程的临界行为.结果表明:声发射事件的三维实时定位直观反映了陶瓷崩碎损伤过程中材料内部微裂纹的萌生、扩展、成核和贯通的损伤演化过程,其定位结果与陶瓷崩口三维几何形貌具有较好的一致性.陶瓷崩碎曲面主要沿着二次多项式的轨迹向陶瓷表面扩展.陶瓷崩碎损伤具有明显的临界行为,声发射计数率和释能率的变化都符合幂律奇异性规律.
关键词:
工程陶瓷
,
崩碎损伤
,
时空演化
,
声发射定位
于俊杰
,
郭伟明
,
林华泰
人工晶体学报
研究了二元助剂Al2O3-Re2O3(Re=La,Nd,Y,Lu)对无压烧结Si3N4陶瓷的相对密度、显微结构及力学性能的影响.结果表明:经1800℃无压烧结后,Si3N4陶瓷试样的相对密度均达到97％以上;以Al2O3-Lu2O3为烧结助剂的Si3N4陶瓷试样具有最高的维氏硬度和抗弯强度,分别为15.2±0.18 GPa和920±5 MPa.
关键词:
Si3N4陶瓷
,
无压烧结
,
相对密度
,
显微结构
,
力学性能
郭伟明
,
吴利翔
,
马提
,
游洋
,
伍尚华
,
林华泰
人工晶体学报
研究了MgO-Al2O3-Re2O3(Re=Lu,Y)三元烧结助剂体系对无压烧结Si3N4陶瓷显微结构和力学性能的影响.研究结果表明,添加MgO-Al2O3-Lu2O3三元助剂制备的Si3N4陶瓷显微结构具有明显的双峰分布,晶粒较粗化,致密度、硬度、弯曲强度、断裂韧性分别为96.4％、14.59 GPa、964 MPa、7.64 MPa·m1/2;而添加MgO-Al2O3-Y2O3三元助剂制备的Si3N4陶瓷具有细化的显微结构,致密度、硬度、弯曲强度、断裂韧性分别为99.9％、15.29 GPa、758 MPa、6.60 MPa·m1/2.
关键词:
Si3N4陶瓷
,
无压烧结
,
显微结构
,
力学性能
,
双峰分布