王建生
,
韩其勇
,
魏寿昆
,
宋波
金属学报
应用Ba蒸气平衡法,在密封Mo反应室内,用自制的TiN和BaS坩埚,进行了纯Fe液中Ba—O,Ba—S,Ba—P平衡的研究。得到反应:BaO_(s)=[Ba]+[O]的标准自由能ΔG°_(wt-％)=188500+38.3T J/mol,e_O~(Ba)=624-1.25×10~6/TBaS_(S)=[Ba]+[S]的标准自由能ΔG°_(wt-％)=469100-111T J/mol,e_S~(Ba)=826-1.64×10~6/T1873K下,反应Ba_3P_2=3[Ba]+2[P]的K_(Ba_3P_2)=7.76×10~(-18),e_(Ba)~P=0.95,ΔG°_(wt-％)=613200 J/mol。
关键词:
Ba
,
O
,
S
,
P
,
liquid iron
,
thermodynamic parameters
杜维玺
,
韩其勇
,
蒋青
,
张钟植
,
钟伟珍
,
刘绍收
金属学报
本文采用电解分离-放射性测量法及显微自射线照相法研究了Ce及S在高纯Fe-C-Si合金各相中的分布和其对石墨形态的影响。实验结果表明:Ce除了与S,O形成夹杂外,首先在石墨中富集;随着合金中Ce含量的增加,石墨中Ce量趋于饱和,大量的Ce以合金化形式存在于铸铁之中;S也在石墨中富集,如合金中S含量继续增加,则以FeS形式存在于共晶团边界;合金中固溶S量极微;石墨形态与Ce在石墨中的吸附和镶嵌程度有关,呈饱和镶嵌吸附时,石墨程球状;呈半饱和态时,石墨为蠕虫状。
关键词:
Ce
,
S
,
Fe-C-Si alloy
,
graphite
邢锦娟
,
彭亮亮
,
冉林涛
,
钱建华
,
许家胜
材料科学与工程学报
doi:10.14136/j.cnki.issn 1673-2812.2017.02.021
以硫脲作为N、S源,尿素作为水解调节剂,水热合成了N/S-TiO2催化剂.采用XRD、SEM、XPS等手段对产品进行了表征.产品分散后,以质量浓度为0.02 g·L-1的甲基橙水溶液为模拟污染物,采用UV-vis光谱,多点BET分析及光催化实验研究了所得产品的光催化活性效果.实验结果表明:S以-+-6价形式进入TiO2晶格取代Ti形成Ti-O-S键,N通过取代晶格中的O形成O-Ti-N键而改变了TiO2能带结构.当煅烧温度为500℃时,水热合成出的产品结晶度较高,粒径较小,约17nm左右.光催化活性实验结果表明:当紫外灯照射时间达到1.5h时,N/S-TiO2催化剂降解甲基橙溶液基本完成,脱色率达到96％/以上.
关键词:
TiO2
,
N
,
S
,
光催化
张殿英
,
李超
,
辛学武
,
钱菁
冶金分析
doi:10.3969/j.issn.1000-7571.2004.z1.063
本文对制样条件、仪器参数、基体干扰、曲线拟合等方面进行了研究.在制样方面,确定了合适的研磨时间、样品粒度、压片时间、压片时所需的压力;通过试验确定了仪器的最佳分析参数.选择与试样基体相匹配的样品,定值后建立工作曲线;对FeO采用经验系数法消除了共存元素的干扰.通过大量生产检验以及与其它方法比对,本方法具有灵敏度高、准确度好、检测限低、测定范围宽等特性,完全能够满足生产需要.
关键词:
X射线荧光光谱法
,
转炉渣
,
CaO
,
SiO2
,
MgO
,
Al2O3
,
FeO
,
TFe
,
P2O5
,
S
Zhijun LIN
,
Meishuan LI
,
Yanchun ZHOU
,
null
,
null
材料科学技术（英文）
Layered ternary ceramics represent a new class of solids that combine the merits of both metals and ceramics. These unique properties are strongly related to their layered crystal structures and microstructures. The combination of atomic-resolution Z-contrast scanning transmission electron microscopy (STEM) and transmission electron microscopy (TEM), selected area electron diffraction (SAED), convergent beam electron diffraction (CBED) represents a powerful method to link microstructures of materials to macroscopic properties, allowing layered ternary ceramics to be investigated in an unprecedented detail. Microstructural information obtained using TEM is useful in understanding the formation mechanism, layered stacking characteristics, and defect structures for layered ternary ceramics down to atomic-scale level; and thus provides insight into understanding the ``Processing-Structure-Property" relationship of layered ternary ceramics. Transmission electron microscopic characterizations of layered ternary ceramics in Ti-Si-C, Ti-Al-C, Cr-Al-C, Zr-Al-C, Ta-Al-C and Ti-Al-N systems are reviewed.
关键词:
Layered ternary ceramics
,
ternary
,
ceramics
,
MAX
,
phase
,
TEM
,
S
Chong TIAN
材料科学技术（英文）
Silicon carbide (SiC) foams with a continuously connected open-cell structure were prepared and characterized for their mechanical performance. The apparent densities of SiC foams were controlled between about 0.4 and 1.3 g/cm3, with corresponding compressive strengths ranging from about 13 to 60 MPa and flexural strengths from about 8 to 30 MPa. Compressive testing of the SiC foams yielded stress-strain curves with only one linear-elastic region, which is different from those reported on ceramic foams in literature. This can possibly be attributed to the existence of filaments with fine, dense and high strength microstructures. The SiC and the filaments respond homogeneously to applied loading.
关键词:
Silicon carbide foams
,
carbide
,
foams
,
Apparent
,
density
,
S
刘清路
,
朱良迪
,
张瑾
,
朱忠其
,
柳清菊
功能材料
doi:10.3969/j.issn.1001-9731.2014.06.007
基于密度泛函理论的第一性原理平面波超软赝势方法研究了纯 TiO2、S 和 La 分别单掺杂及共掺杂锐钛矿相TiO2的晶体结构、电子结构、光学性质及带边位置,结果表明,S掺杂后TiO2的晶格常数、原子间的键长和原子电荷都发生了变化,导致掺杂后的八面体偶极矩增加,从而有利于光生电子-空穴对的分离,提高TiO2的光催化性能；S掺杂TiO2禁带中出现杂质能级,从而将 TiO2的光谱响应红移至可见光区；La掺杂TiO2杂质能级出现在导带而非禁带中,带隙有所减小,吸收光谱的阈值波长发生了一定的红移；而S、La共掺杂TiO2的光谱响应范围向可见光区明显拓展,且氧化还原能力增强,因此 S、La 共掺杂可显著提高TiO2光催化性能。
关键词:
锐钛矿相TiO2
,
第一性原理
,
S
,
La 共掺杂
,
光催化性能
徐启迪
,
黄娇
,
姚美意
,
彭胜
,
张金龙
,
彭剑超
,
周邦新
,
沈剑韵
稀有金属材料与工程
在Zr-0.70Sn-0.35Nb-0.30Fe(质量分数,％)合金成分基础上添加26～570 μg/g的S制备成实验合金,用SEM、TEM及其配置的EDS研究了S含量对合金中第二相成分及晶体结构的影响.结果表明:不加S的重熔合金中的第二相均为密排六方结构的Zr(Nb,Fe)2,添加S以后合金中出现了正交结构的Zr3Fe第二相,并随着S含量的增加,Zr3Fe的数量也相应增多;添加的S含量为190 μg/g时,合金中还出现了四方结构的Zr9S2第二相,并随着S含量的进一步增加,Zr9S2第二相的数量增多;同一成分合金中随第二相粒子尺寸的增大,第二相中的Nb/Fe比值逐渐降低.本研究制备的含S锆合金中,固溶在α-Zr基体中的最大S含量在26～190 μg/g之间,超过固溶含量的S以Zr9S2第二相析出,并没有进入其它第二相中.
关键词:
锆合金
,
显微组织
,
第二相
,
S
吐尔逊·艾迪力比克
,
巴合提古丽·阿斯里别克
,
艾尔肯·斯地克
功能材料
doi:10.3969/j.issn.1001-9731.2013.17.002
采用固相法制备了 S、Eu2 O3共掺杂天然方钠石的橘黄荧光粉末 Na8 Al6 Si6 O24 Cl2∶S2-,Eux 3+(密度x=1%、3%、5%和10%(质量分数))。用 XRD对其结构进行了表征。研究了室温和低温下该粉末的激发光谱、发射光谱特性。在265nm 激发下的发射光谱包括由 Eu3+中4f6(5 D0)→4f6(7 FJ )(J=0、1、2、3、4)跃迁产生的、峰值在581~707nm 间的光谱带和由Mn2+的4T1→6A1跃迁产生的、峰值在496nm 的光谱带。改变方钠石掺杂的两种元素的质量分数研究了方钠石的发光特性。实验结果表明,S2-和 Eu3+离子之间有能量抵消。
关键词:
方钠石
,
光致发光
,
Eu
,
S