A study was conducted to examine the isothermal oxidation behavior of a new Ni-Cr-W-Al alloy in air at 1250°C with different time. Oxidation kinetics was determined from weight-change measurements. The microstructure and composition of the oxide scale were investigated by means of scanning electron microcopy and X-ray diffraction. The results showed that the oxide scales of the alloy were a compact and continuous outer Cr2O3 and NiCr2O4 layer and an inner Al2O3 layer that was in dendrite shape. Oxides scales with good adherence were formed on the surface of the alloy, which made the alloy perform excellent high-temperature oxidation resistance.
关键词:
Oxidation kinetics
,
null
,
null
Y.C. Ma
材料科学技术（英文）
A study was conducted to examine the isothermal oxidation behavior of a new Ni-Cr-W-Al alloy in air at 1250°C with different time. Oxidation kinetics was determined from weight-change measurements. The microstructure and composition of the oxide scale were investigated by means of scanning electron microcopy and X-ray diffraction. The results showed that the oxide scales of the alloy were a compact and continuous outer Cr2O3 and NiCr2O4 layer and an inner Al2O3 layer that was in dendrite shape. Oxides scales with good adherence were formed on the surface of the alloy, which made the alloy perform excellent high-temperature oxidation resistance.
关键词:
Oxidation kinetics
,
null
,
null
Mengjin LI
,
Xiaofeng SUN
,
Hengrong GUAN
,
Xiaoxia JIANG
,
Zhuangqi HU
材料科学技术（英文）
(Ni,Pd)Al coating, prepared by low pressure pack cementation on the Ni-base superalloy M38 where Pd-20 wt pct Ni alloy was predeposited, consists of a single β-(Ni,Pd)Al phase. The initial isothermal oxidation behavior of (Ni,Pd)Al coating was investigated by TGA, XRD, SEM/EDS at 800-1100℃. Results show that oxidation kinetics accord preferably with parabolic law at 800, 900 and 1100℃, but not at 1000℃. β-Al2O3 was observed at 800-1100℃. It is found that Pd plays an important role in accelerating the diffusion of Ti from the substrate to the coating surface in the aluminide coating.
关键词:
(Ni
,
null
,
null
,
null
,
null