林一坚
,
胡坚
,
尤云龙
,
井春永
,
郁泉琴
金属学报
液态急冷Fe_(70)Cr_(18)Mo_2SiB_2在700—1150℃退火中可生成M_2B,M_3B_2和M_(23)B_6硼化物。M_2B随温度的升高,由Fe_2B为主,经Fe_2B和Cr_2B的平衡共存,逐步被Cr_2B所取代。Cr_2B可由Fe_2B通过原子置换和结构调整转变而成,残余Fe_2B以层错形式的薄片夹在(Cr,Fe)_2B(100)面之间,M_3B_2实际为Mo_(1+x)(Fe,Cr)_(2-x)B_2(0≤x≤1),x随温度上升而连续增大。
关键词:
FeCrMoSiB合金
,
M_2B
,
M_3B_2
,
M_(23)B_6
LIN Yijian HU Jian YOU Yunlong JING Chunyong YU Quanqin Shanghai Iron and Steel Research Institute
,
Shanghai
,
China LIN Yijian Measuring and Testing Centre
,
Shanghai Iron and Steel Research Institute
,
Shanghai 200940
,
China
金属学报(英文版)
The formation of borides M_3B_2 M_2B_2 and M_(23)B_6 may be carried out from the melt-quenched Fe_(70)Cr_(18)Mo_2SiB_9 during 700—1150℃ annealing.As the temperature raising,the M_2B,the majority being Fe_2B.may be gradually replaced by Cr_2B via the co-existence between Fe_2B and Cr_2B.The Cr_2B may be formed by trans formation of Fe_2B through the atomic substitu- tion and structural adjustment.The thin slice of remaining Fe_2B is sandwiched between(100) faces of(Cr,Fe)_2B as stacking fault.The M_2B_2 is virtually composed of the Mo_(1+x)(Fe,Cr)_(2-x)B_2 where x(0≤x≤1)increases with the increase of temperature.
关键词:
FeCrMoSiB alloy
,