针对超超临界机组中863 K服役20000 h的HR3C再热器管材及与其具有相同Larson-Miller参数值的923 K时效1100 h HR3C管材,开展显微组织结构老化及力学性能衰减的对比研究.结果表明,服役环境的不同导致服役态HR3C钢管的内外侧显微组织结构产生差异.服役态HR3C内侧的显微组织结构和力学性能与时效态的基本相同;然而,服役态钢管外侧的结构损伤程度比时效态钢管更严重.因此,基于Larson-Miller参数的人工时效方法只能在一定条件下模拟USC机组中钢管的结构老化.
关键词:
HR3C耐热钢
,
Larson-Miller参数
,
结构损伤
,
力学性能
R.C.Yang
,
K.Chen
,
H.X.Feng
,
H.Wang
金属学报(英文版)
Based on the analysis and processing on relative empirical formula and data, C-values in Larson-Miller (P) expression, P = T(C + lgt), have determined for pearlitic heat resistant steel 12Cr1Mo V and 15 CrMo (20. 62 and 20. 30). The simulation experiments of high temperature aging, heated from 1.5 to 873 hours, have been designed and performed for its verification. And in combination with published information and the present nearly quantitative works, it has further been verified that both the degradations of microstructures and mechanical properties show a good accuracy and practicability using the Larson-Miller parameter with the present determined C-values. Finally, the effects of carbon content on C-value are analyzed by the empirical electron theory of solids and molecules (EET).
关键词:
pearlitic heat-resistant steel
,
null
,
null