Weizhong JIN
,
Sen YANG
,
Hiroyuki KOKAWA
,
Zhanjie WANG
,
Yutaka S.Sato
材料科学技术（英文）
Intergranular stress corrosion crack susceptibility of austenite stainless steel was evaluated through threepoint bending test conducted in high temperature water. The experimental results showed that the frequent and efficient introduction of low energy coincidence site lattice boundaries through grain boundary engineering resulted in an apparent improvement of the intergranular stress corrosion crack resistance of austenite stainless steel.
关键词:
Intergranular stress corrosion cracking
,