Zhengang Liu Guoyin Zu Hongjie Luo Yihan Liu Guangchun Yao
材料科学技术（英文）
Al alloy matrix composites reinforced with copper-coated graphite particle have been prepared by melt stirring process in this work. The effect of the addition of Mg on distribution of the graphite particles has been investigated. Scanning electron microscopy (SEM) was used to observe the micro-morphology of Al alloy matrix composites reinforced with graphite particles. Meanwhile, the content of graphite was analyzed in the different position of casting by dissolution method and the mechanical properties of the composites were detected. The results show that the content of graphite increase with increasing Mg content; the graphite particles distribute uniformly in the particle reinforced metal matrix composites (PMMC) with 0.6 wt pct Mg; however, the agglomeration of the graphite particles is observed obviously in the matrix when Mg content is more than 1.0 wt pct. In addition, the proper Mg addition amount is beneficial to enhance the mechanical properties of the graphite particles reinforced Al alloy matrix composites and the abrasion resistance of the materials due to a reduce friction coefficient.
关键词:
Graphite particles
,
铝合金基复合材料；分布；镁；力学性能
Peng ZHANG
,
Yunhui DU
,
Hanwu LIU
,
Daben ZENG
,
Jianzhong CUI
,
Limin BA
材料科学技术（英文）
The electromagnetic-mechanical stirring technology was used to prepare QTi3.5-15/graghite slurry. The distribution of graphite particles in QTi3.5-15/graghite slurry was studied using cold quenching method. The results show that solid fraction of QTi3.5-15/graphite slurry increases with the decreasing of stirring temperature. There is a linear relationship between solid fraction and stirring temperature. With the increasing of solid fraction, the distribution of graphite particles in slurry becomes uniform gradually. When the solid fraction is larger than 45%, the rising of graphite particles in slurry can be restricted, and QTi3.5-15/graghite slurry with uniform distribution of graphite particles can be prepared.
关键词:
null
,
null
,
null