王隆保
金属学报
研究了机械研磨对退火变脆Fe_(75)Si_(10)B_(15)金属玻璃的弛豫过程,晶化行为及脆韧性转变的影响。发现退火变脆的Fe_(75)Si_(10)B_(15)金属玻璃,经不同时间机械研磨,Curie温度T_C逐渐回落,总的弛像焓ΔH_?逐渐回升。在DSC曲线上观察到明显的玻璃转变温度T_(g_1)和一个附加的宽放热峰T_(x_1),随着研磨时间的增加,T_(x_1),T_(x_1),T_C同步降低,与T_(x_1)对应的放热面积ΔH_(x_1)逐渐增大,并在片状粒子表面形成切变带以及与其对应的剪切带,玻璃在退火过程中失掉的韧性逐渐得到恢复。
关键词:
机械研磨
,
Fe_(75)Si_(10)B_(15)
,
metallic glass
WANG Longbao State Key Laboratory of Rapidly Solidified Non-Equilibrium Alloys
,
Institute of Metal Research Academia Sinica
,
Shenyang
,
ChinaDAVIES H A School of Materials
,
University of Sheffield
,
U.K
金属学报(英文版)
Studies were made of the effect of mechanical pulverization on relaxation,crystallization and brittle-ductile transition of the anneal-embrittled Fe_(75)Si_(10)B_(15) metallic glass rib- bon.Results show that the Curie temperature,T_C,decreases and the total enthalpy of relaxation increases gradually with variation of pulverized time.DSC traces reveal an extra exothermic peak,T_X_1,and a distinct glass transition endothermic peak,T_g_1,with increasing pulverized time,T_C,T_X_1,and T_g_1 decrease simultaneously,and the exother- mic peak area corresponding to T_X_1 increases gradually.The surface slip-steps of flaky particles and their corresponding shear are produced by pulverizing the pre-embrittled amorphous glass.The lost ductility of the glass may restore during annealing.
关键词:
mechanical pulverization
,
null
,
null
,
null