Microstructure observation and dynamic mechanical analysis were carried out to investigate the precipitation and responding damping behaviors of AZ31 magnesium alloy. All the strain amplitude-dependent damping curves of the aged alloys are located between the curves of solutionized and as-cast alloys, although they have different critical strain amplitudes. The G-L theory is employed to explain the damping mechanism involving the interaction between the dislocation and the precipitated phase. In addition, a damping peak is observed at temperatures close to 330 ℃ for AZ31 magnesium alloy, which is related to the β-Mg17Al12 phase dissolution.
关键词:
Magnesium alloys
,
null
,
null
,
null
,
null
张青
,
成来飞
,
王芙愿
,
张立同
新型炭材料
以化学气相渗透(CVI)技术制备的2D C/SiC复合材料为研究对象,探讨复合材料在700、1000和1300益空气环境中发生不同形式和不同程度氧化损伤后的阻尼行为变化。采用扫描电子显微镜( SEM)观察和分析复合材料的微结构损伤,采用动态力学分析仪(DMA)测试复合材料损伤前后的阻尼性能。结果表明：在700益和1000益空气环境中,随着氧化时间的延长,2D C/SiC复合材料的阻尼性能先增大后降低；而在1300益空气环境中,阻尼性能变化较小,且随氧化时间的延长未表现出明显的规律性。这是由于C/SiC复合材料的阻尼由炭纤维、热解炭界面和碳化硅基体,以及它们之间的相互作用共同形成。炭纤维和热解炭界面的氧化损伤会对复合材料阻尼特性产生两种影响机制,其一是使复合材料阻尼性能增大的机制,主要来自于热解炭界面相损耗引起的界面结合强度降低；其二是使复合材料阻尼性能降低的机制,主要来自于纤维的损耗和界面区的过度破坏。而碳化硅氧化生成的二氧化硅主要是通过影响碳相的氧化程度来影响复合材料的阻尼性能。
关键词:
C/SiC复合材料
,
阻尼行为
,
氧化损伤