NING Yuantao ZHO U Xinming LI Yongnian Kunming Institute of Precious Metals
,
Kunming
,
China
金属学报(英文版)
The 0,05—0.08 mm thick splat foils of Ag-Tb alloy,containing Tb up to 10 at.-%,were made by the hammer-anvil technique.The cooling rate was in order of 10~6 K/s.The metastable extension of solid solubility of Tb in the alloy was measured to be up to 5 at.-% by lattice parameter method.The secondary phase in metastable eutectic structure was identi- fied as Ag_3Tb from diffraction pattern.The microstructure and micro-defect in as-quenched Ag-Tb splat foil were also observed.
关键词:
rapid solidification
,