Electron enregy loss spectroscopy (EELS) and energy filtering transmission electron microscopy (EFTEM) investigation on 2.25Cr-1Mo steel was carried out to understand the nature of evolution of secondary carbides. The filtered images obtained from two different ageing treatments indicate that the steel evolves to a more stable carbide namely M23C6 in comparison to M2C. Microchemical information was generated from EELS spectra. Suitable choice for estimating the microchemical state was discussed. To evaluate the behaviour of ageing an elemental ratio of Fe to Cr is employed.
关键词:
Ferritic steels
,
Steels
,
2.25Cr-1Mo
,
steels
,
EFTEM
张喜亮
,
刘涛
,
崔国华
,
周昌玉
,
刘争
,
张维
材料工程
doi:10.11868/j.issn.1001-4381.2014.10.011
根据溶质晶界偏聚理论和原子扩散原理研究了2.25Cr 1Mo钢服役12年后磷晶界偏聚行为及脱脆处理工艺.采用俄歇电子能谱实验对溶质原子的晶界偏聚程度进行了测试分析.结果表明:对于已脆化的2.25Cr 1Mo钢,存在临界脆化温度,且脆化程度越高,临界脆化温度越低;高于临界脆化温度数小时的保温即可消除脆化现象,即2.25Cr 1Mo钢的脱脆速率远大于脆化速率.
关键词:
脱脆
,
2.25Cr-1Mo钢
,
晶界偏聚
,
磷
刘涛
,
张喜亮
,
卢宝城
,
周昌玉
机械工程材料
对加氢反应器用2.25Cr-1Mo钢进行了回火脆化并充氢处理；通过冲击试验机、俄歇电子能谱仪及扫描电镜等研究了2.25Cr-1Mo钢在回火脆化与氢脆联合作用下的脆化情况;结合晶界偏聚理论,计算了在不同回火及充氢处理后杂质磷原子在晶界上的偏聚量.结果表明:试验钢的脆化程度不能用显微组织、硬度的变化来评价;在回火温度范围内,随着回火时间的延长,试验钢回火脆化的程度逐渐增大,氢进一步增加了其脆化程度,并且回火脆化与氢脆联合作用下的脆化程度要远大于回火脆化的;氢增大了试验钢中杂质原子磷的扩散系数,进而促进磷原子向晶界偏聚,这是充氢加重回火脆化的主要原因.
关键词:
俄歇电子能谱
,
回火脆化
,
2.25Cr-1Mo钢
,
氢脆
,
晶界偏聚