金属学报(英文版)
The damping capacities (Q-1) of high silicon (6wt%) Zinc-27wt% Aluminia alloy prepared by spray deposition and conventional casting process were investigated. Three methods, free-decay, half-power band width and phase angles difference, have been ased to measure the damping capacities of the experimental materiale. The experimental results indicate that the damping capacity of spray deposited material is 3.7times larger than that of the conventional casting alloy ZA27 The machanism for its improvement was aiso investigated from a microstructvre viempoint.
关键词:
high damping alloy
,
null
,
null
,
null
侯小虎
,
白朴存
,
沈元国
,
李博
材料热处理学报
采用拉伸实验、硬度测试、高分辨透射电子显微镜(HRTEM)、扫描电镜(SEM)等方法研究了回归及回归再时效处理对喷射沉积高Zn(质量分数为12％)7000系铝合金的微观组织及力学性能的影响.结果表明,该合金经峰值时效处理(120℃×14 h)后,晶内主要强化相为GPⅡ区,晶界析出相呈连续分布;经回归处理(180℃×0.5h)后,晶内主要强化相为较小的η'相,晶界析出相明显粗化;采用回归再时效处理(120℃×14 h+180℃×0.5 h+120℃×14 h)后,晶内析出物为亚稳定的η'相和稳定的η相,晶界析出相为不连续分布的η相;对η相高分辨像进行解卷处理,利用jems软件构建η相晶胞并模拟其高分辨像,最终确定η相各原子所在的位置.回归时效实验合金的抗拉强度达到890 MPa,伸长率为9.2％,断口为沿晶和穿晶混合断裂.
关键词:
7000系铝合金
,
喷射沉积
,
回归再时效
,
微观组织
,
解卷处理