Density functional theory was employed to investigate the bismuth segregation at Cu/Cu3Sn(010) interface. Five initial constructions were introduced by adopting the adhesion energy criterion. Among them, the so-called "between-Cu" construction in which the interface Cu atoms of Cu slab locate along Cu-Cu bond direction in Cu3Sn slab was found to be the most energy-favored at an adhesion energy of 1.96 J/m2. Based on this construction, five possible segregation sites were examined, and the most likely segregation site was determined with adhesion energy as low as 1.06 J/m2, which was almost half of the initial one. Comparing with other sites' adhesion energies, it was concluded that size effect took a large part in embrittlement. The analyses of atomic structure and electronic density revealed that the slabs shifted away from interfaces due to bismuth segregation, and the atoms around Bi atom were pressed away. This calculated work agreed qualitatively with reported experimental results.
关键词:
First-principles calculation
,
segregation
,
Bismuth
,
interface
,
SnBi solder.
刘皓
,
李克智
,
李贺军
,
卢锦花
,
翟言强
无机材料学报
doi:10.3724/SP.J.1077.2007.00968
借助偏光显微镜、扫描电镜、透射电镜以及力学性能测试研究了微观结构对中间相沥青基炭/炭复合材料力学性能的影响. 结果表明: 基体炭在偏光显微镜下呈现出光学各向异性, 在SEM和TEM下呈片层条带状结构. 基体炭与纤维之间的界面不连续, 为“裂纹型”界面. 材料受载破坏时裂纹通过改变扩展路径而延缓其扩展速度, 在纤维-基体界面处以及基体炭层片之间引起滑移, 在断口形貌上体现出断裂台阶适中且与纤维拔出交替进行, 表现出韧性破坏的断裂特征. 材料具有较高的力学性能, 抗弯强度达到257MPa, 断裂韧性达到11.4MPa·m 1/2.
关键词:
炭/炭复合材料
,
mesophase pitch
,
microstructure
,
interface
,
mechanical properties
黄福龙
,
戴红莲
,
方园
,
单学智
,
李世普
无机材料学报
doi:10.3724/SP.J.1077.2007.00333
首先采用开环聚合合成了PDLLA, 液相-沉淀法合成了HA超微粉, 然后采用液相吸附法制备了HA/PDLLA复合材料. 以纯PDLLA进行对照, 对HA/PDLLA复合材料进行体外降解实验和体内植入实验, 并进行扫描电镜观察. 结果表明HA/PDLLA复合材料较单纯PDLLA材料的降解速度减慢, 机械强度升高, 避免了过早的丧失力学强度. HA颗粒从材料表面脱落后, 成纤维细胞向组织内长入, 并伴有少量新生骨痂的形成, 显示HA/PDLLA复合材料具有良好的降解性能, 一定的成骨性和骨连接性. 24周时, HA/PDLLA材料被组织分隔包裹, 新生骨组织长入材料, 骨愈合情况良好, 具有足够的强度保证实验性松质骨骨折正常愈合.
关键词:
羟基磷灰石
,
poly DL-lactide
,
liquid phase absorption method
,
biodegradability
,
interface
孙万昌
,
李贺军
,
卢锦花
,
白瑞成
,
黄勇
无机材料学报
采用快速化学液相气化渗透法制备了C/C复合材料;利用扫描电子显微镜观察了材料的断口形貌特征;研究了不同层次界面状态对C/C复合材料力学行为及断裂模式的影响. 研究表明:束内纤维与基体间结合要适度,既不能过强也不能过弱,保证材料具有高强度同时又具有一定塑韧性;当碳布层间或束间的基体热解碳与纤维柬表面之间残余孔隙量较多或者结合较弱时,则裂纹沿碳布层表面的纤维与基体热解碳之间扩展而分层;热解碳碳层面排列的越紧密,层面间的结合强度越高,则倾向于在基体热解碳内形成齐茬形断面;若碳层面之间存在过多间隙或结合较弱,则倾向于沿碳层面剥离而分层.
关键词:
碳/碳复合材料
,
rapid densification
,
interface
,
mechanical behavior
李嘉
,
尹衍升
,
刘俊友
,
范润华
无机材料学报
根据热力学原理,考察了Fe-Al系金属间化合物与ZrO2陶瓷基体的化学相容性。结果表明,当Fe-Al金属间化合物中Al<42at％时,Fe-Al金属间化合物与ZrO2基体不易发生化学反应。XRD、SEM及HREM分析验证了此结论。HREM观察表明Fe3Al与基体3Y-TZP之间界面干净,无反应层和过渡层的存在,Fe3Al与ZrO2界面两侧的原子排列不是一一对应的,只是部分互相匹配,形成半共格关系。界面上品面间错配度δ=30％,界面上存在着错配位错。
关键词:
复合材料
,
chemical compatibility
,
thermodynamic calculation
,
interface
孙万昌
,
李贺军
,
卢锦花
,
白瑞成
,
黄勇
无机材料学报
采用快速化学液相气化渗透法制备了C/C复合材料;利用扫描电子显微镜观察了材料的断口形貌特征;研究了不同层次界面状态对C/C复合材料力学行为及断裂模式的影响. 研究表明:束内纤维与基体间结合要适度,既不能过强也不能过弱,保证材料具有高强度同时又具有一定塑韧性;当碳布层间或束间的基体热解碳与纤维柬表面之间残余孔隙量较多或者结合较弱时,则裂纹沿碳布层表面的纤维与基体热解碳之间扩展而分层;热解碳碳层面排列的越紧密,层面间的结合强度越高,则倾向于在基体热解碳内形成齐茬形断面;若碳层面之间存在过多间隙或结合较弱,则倾向于沿碳层面剥离而分层.
关键词:
碳/碳复合材料
,
rapid densification
,
interface
,
mechanical behavior