H.S. Liu B. Zhang G.P. Zhang
材料科学技术（英文）
Al/Mg alloy multilayered composites were produced successfully at the lower temperature (280°C) by accumulative roll bonding (ARB) processing technique. The microstructures of Al and Mg alloy layers were characterized by scanning electron microscopy and transmission electron microscopy. Vickers hardness and three-point bending tests were conducted to investigate mechanical properties of the composites. It is found that Vickers hardness, bending strength and stiffness modulus of the Al/Mg alloy multilayered composite increase with increasing the ARB pass. Delamination and crack propagation along the interface are the two main failure modes of the multilayered composite subjected to bending load. Strengthening and fracture mechanisms of the composite are analyzed.
关键词:
Accumulative roll bonding (ARB)
,
Al/Mg alloy multilayered composite
,
Ultra-fine grains
,
Hardness
,
Bending properties
H.S. Liu B. Zhang G.P. Zhang
材料科学技术（英文）
Al/Mg alloy multilayered composites were produced successfully at the lower temperature (280°C) by accumulative roll bonding (ARB) processing technique. The microstructures of Al and Mg alloy layers were characterized by scanning electron microscopy and transmission electron microscopy. Vickers hardness and three-point bending tests were conducted to investigate mechanical properties of the composites. It is found that Vickers hardness, bending strength and stiffness modulus of the Al/Mg alloy multilayered composite increase with increasing the ARB pass. Delamination and crack propagation along the interface are the two main failure modes of the multilayered composite subjected to bending load. Strengthening and fracture mechanisms of the composite are analyzed.
关键词:
Accumulative roll bonding (ARB)
,
Al/Mg alloy multilayered composite
,
Ultra-fine grains
,
Hardness
,
Bending properties