The microstructure and piezoelectric properties of Pb[(Zr0.52Ti0.48)0.95(Mn1/3Nb2/3)0.05]O3 (PMnN-PZT) ceramics have been investigated at different sintering temperatures from 1070℃ to 1280℃. The experimental results suggest that grain sizes and electromechanical properties of the ceramics show strong sintering temperature dependences. Double polarization to electric field (P-E) loops of the PMnN-PZT ceramics are assumed to be the result of the pinning effect of the defect dipoles. The results obtained through X-ray photoelectron spectrum suggest that sintering temperature affects valence of the Mn ion and quantity of oxygen vacancies. Hence, a proper explanation is proposed to illustrate the fluctuation of mechanical quality factor (Qm) due to the sintering temperature.
关键词:
Sintering temperature
,
压电特性
,
铌锰锆钛酸铅
,
氧空位
李宝山
,
朱志刚
,
李国荣
,
殷庆瑞
,
丁爱丽
无机材料学报
运用XRD、SEM、TEM、XPS等实验手段,研究了烧结温度对0.05PMnN-0.95PZT (PMnN—PZT)压电陶瓷微观结构、压电性能及锰元素价态的影响.实验结果显示:随烧结温度的降低平均晶粒尺寸减小,四方度也随之减小;机电耦合系数(kp)随烧结温度的升高而提高, 而机械品质因子(Qm)却呈波浪状变化. XPS及TEM实验分析证明:PMnN—PZT陶瓷在烧结过程中出现明显的液相烧结和成分偏离,低温烧结诱导了Mn2+的出现,产生更多的氧空位,从而使低温烧结下的样品Qm值不致降低.
关键词:
铌锰锆钛酸铅
,
sintering temperature
,
valency of Mn
,
oxygen vacancies
李宝山
,
朱志刚
,
李国荣
,
殷庆瑞
,
丁爱丽
无机材料学报
doi:10.3321/j.issn:1000-324X.2005.04.037
运用XRD、SEM、TEM、XPS等实验手段,研究了烧结温度对0.05PMnN-0.95PZT(PMnN-PZT)压电陶瓷微观结构、压电性能及锰元素价态的影响.实验结果显示:随烧结温度的降低平均晶粒尺寸减小,四方度也随之减小;机电耦合系数(kp)随烧结温度的升高而提高,而机械品质因子(Qm)却呈波浪状变化.XPS及TEM实验分析证明:PMnN-PZT陶瓷在烧结过程中出现明显的液相烧结和成分偏离,低温烧结诱导了Mn2+的出现,产生更多的氧空位,从而使低温烧结下的样品Qm值不致降低.