Tingdong ZHOU
金属学报(英文版)
FeSiAlCr alloy powders were prepared by mechanical alloying, the milling time were 20 h, 40 h, 60 h and 80~h, respectively. Powders morphology was studied by SEM. Microstructure of powders milled for various times were analyzed by XRD. The complex permittivity and complex permeability of four powders were tested in the frequency range from 0.5 to 18 GHz, and their microwave absorption properties were analyzed. It was found that the particle size of powders milled for 80~h was less than 2μm. Silicon and aluminum atoms were dissolved into the crystal lattice of iron, and chromium atoms can form alloy with iron atoms. The minimum peak value of reflectivity can reach to -11.3 dB at the frequency of 4.3 GHz for 80 h milling powders, and the other one was -6 dB at 16.5 GHz.
关键词:
FeSiAlCr alloy
,
固溶体
,
电磁参数
,
反射率
,
机械合金化
曾国勋
,
葛鹰
,
张海燕
,
贺春华
,
陈天立
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2010.01.020
在传输/反射法测量电磁参数的基础上,分析了传统的传输/反射法在电介质微波电磁参数计算中的局限性,采用时域门技术,测试了空气、聚乙烯石蜡和BaM型铁氧体等材料的电磁参数.结果显示时域门技术可显著提高材料的测量精度和稳定性.
关键词:
矩形波导
,
传输/反射法
,
电磁参数
,
时域门
方庆玲
,
李效东
,
车仁超
,
李公义
稀有金属材料与工程
以二茂铁和苯为原料采用CVD技术制各了定向、长为15～160 μm铁/碳纳米管雷达波吸收剂,考察了反应温度,保温时间等对其生长状况的影响.采用扫描电镜(SEM)、高分辨透射电子显微镜(HRTEM)、x-射线光电子能谱(XPS)对所得产物进行了形貌、组成、结构表征.结果表明产物有较高的铁填充率,铁元素是以α-Fe晶型包覆在多壁碳纳米管中;吸收剂密度为2.4～2.6 g/cm3,电磁参数在2～18 GHz范围内呈现良好的频散效应,低频段尤为显著.
关键词:
铁/碳纳米管
,
二茂铁
,
微观结构
,
电磁参数
黄英
,
赵利
,
时刻
,
王利
,
赵文涛
稀有金属材料与工程
通过化学镀方法在玻璃纤维表面沉积了Ni-Fe-W-P合金,所用镀液经钯盐法测试,稳定性很好,所得镀合金玻璃纤维经热震实验后表面无鼓泡、起皮现象,说明镀层的抗冲击强度高,结合力良好.利用扫描电镜观察了镀层的表面形貌,同时使用x射线能谱仪对镀层成分含量进行了分析,镀层中钨的质量分数最大可达22.2%,并得出了硫酸镍、硫酸亚铁、钨酸钠浓度对镀层导电性能的影响情况,制备的镀合金玻璃纤维电阻率为28.3×10-3Ω·cm.对玻璃纤维合金层进行的XRD分析表明,在镀态下为非晶态结构,玻璃纤维热稳定性好,适宜的工作温度范围低于250.C.最后对所得Ni-Fe-W-P合金玻璃纤维的电磁参数进行了初步的测定与分析,所得镀金属玻璃纤维的磁损耗为0.054 75;介电损耗为2.184 24,镀层合金为软磁性材料.
关键词:
玻璃纤维
,
化学镀
,
Ni-Fe-W-P合金
,
电阻率
,
电磁参数
翟青霞
,
黄英
航空材料学报
doi:10.3969/j.issh.1005-5053.2011.6.010
为了比较不同形态的镧掺杂纳米锶铁氧体复合材料电磁性能的优劣,分别以溶胶-凝胶法制备了稀土镧掺杂纳米锶铁氧体( SrLa0.4Fe11.6O19)颗粒、原位复合技术制备了镧掺杂锶铁氧体/聚苯胺(SrLa0.4Fe11.6 O19/PANI)纳米复合颗粒,静电自组装法制备了镧掺杂锶铁氧体/聚苯乙烯磺酸钠( SrLa0.4Fe11.6O19/PSS)20、镧掺杂锶铁氧体/聚苯乙烯磺酸钠/聚苯胺( SrLa0.4Fe11.6 O19/PSS/PANI)8纳米复合多层膜.用XRD,FTIR,FETEM,XPS,矢量网络分析,VSM研究了镧掺杂锶铁氧体/聚苯胺纳米复合材料结构和性能.结果表明:在9.21GHz附近,材料的损耗角正切大小排序为:( SrLa0.4Fe11.6 O19/PSS/PANI)8复合多层膜＞SrLa0.4 Fe11.6O19/PANI复合颗粒＞SrLa0.4 Fe11.6 O19颗粒；(SrLa0.4Fe11.6O19/PSS/PANI)8复合多层薄膜比颗粒材料具有更高的饱和磁化强度Ms和矫顽力Hc.(SrLa0.4Fe11.6O19/PSS/PANI)8纳米复合多层膜具有优良的电磁性能.
关键词:
镧掺杂锶铁氧体
,
聚苯胺
,
静电自组装
,
电磁参数
高敬伟
,
姚寅芳
,
黄梦龙
,
李光
,
江建明
材料导报
以十二烷基苯磺酸钠(SDBS)为掺杂剂采用乳液聚合法合成了不同掺杂率的聚吡咯.通过元素分析n(S)/n(N)表征了所得聚吡咯的掺杂率,并测试了不同掺杂率的聚吡咯的电导率,发现电导率随掺杂率的增加先增大后下降.以掺杂聚吡咯为吸波荆制备了环氧树脂复合材料,并测试了其在X波段的电磁参数.由单层平行板模型 计算出复合材料的吸波性能,结果表明,当n(SDBS)/n(Py)=0.2(Py为吡咯单体)的掺杂聚吡咯(PPy)在复合材料中的含量为20%时吸波性能最好,即当样品厚度为2.3mm时其反射损耗最小,达到-14.8dB,且在9.5～11.6GHz的频宽范围均低于-10dB.
关键词:
十二烷基苯磺酸
,
聚吡咯
,
电磁参数
,
掺杂
,
吸波性能
冯永宝
,
丘泰
,
张军
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2005.04.008
采用羰基铁粉为吸收剂、三元乙丙橡胶(EPDM)为基体,研究了羰基铁粉用量对微波吸收贴片力学与电磁性能的影响;利用扫描电镜探讨了复合材料的微观结构.结果表明:随着羰基铁粉在橡胶基体中填充量的增加,其力学性能和电磁性能均有较大程度的提高;断面的扫描电镜照片表明,羰基铁粉与三元乙丙橡胶界面结合性能较好,在基体中分散较均匀.利用基于改进遗传算法的优化软件对以羰基铁粉为吸收剂的微波吸收贴片吸波性能进行优化预测,优化结果表明:应用配比为w(羰基铁):w(EPDM)=1 050:100,制成厚度为0.8 mm的单层吸波贴片,可以实现在8～18 GHz范围内反射率＜-8dB;以配比为w(羰基铁):w(EPDM)=1 050:100的吸波贴片0.6 mm作为内层材料,以配比为w(羰基铁):w(EPDM)=150:100的吸波贴片1.5 mm作为外层材料,制备成总厚度为2.1 mm的双层吸波贴片,可以实现在8～18 GHz范围内反射率＜-12 dB.
关键词:
羰基铁粉
,
三元乙丙橡胶
,
微波吸收贴片
,
电磁参数
,
力学性能
孙国亮
,
郑文伟
,
程海峰
材料导报
首次采用电镀法制备片状磁性吸收剂,用SEM、XRD等手段对其进行表征.为减少吸收剂表面氧化,提高吸收剂吸波性能,采用溶胶-凝胶法和磷化法两种不同的表面处理工艺对吸收剂进行处理.用网络分析仪测试了耒处理吸收剂样品和处理过的吸收剂样品2～18GHz的电磁参数,并对比了其处理前后的SEM照片.结果表明:通过表面处理,片状吸收剂的磁导率有所上升,进而能够提高其吸波性能;比较这两种表面处理工艺,溶胶-凝胶法要优于磷化法.
关键词:
电镀铁
,
片状吸收剂
,
表面处理
,
电磁参数
方志刚
,
李处森
,
孙家言
,
张劲松
宇航材料工艺
doi:10.3969/j.issn.1007-2330.2010.01.021
利用网络分析仪连接矩形谐振腔组成材料电磁参数微扰法测试系统.由谐振腔微扰理论出发,得到以托管装载小样品测试时复介电常数和复磁导率的计算公式.对碳泡沫进行电磁参数测试.结果表明,随着碳泡沫电导率的增加,其介电常数缓慢增加,电损耗先增加后减小,而磁损耗不断增加.碳泡沫具有介电常数小、电损耗大、随电导率增加而增加的非本征磁损耗,这种独特的电磁损耗特征使得碳泡沫有用作宽频带高温结构吸波材料的可能性.
关键词:
吸波材料
,
碳泡沫
,
电磁参数
,
微扰法
朱红
,
赵璐
,
郭佳
,
郭洪范
功能材料
用联氨作为还原剂,通过化学镀的方法在碳纤维粉基体上包覆纯金属镍层,获得一种新的功能复合材料.SEM电镜和EDX能谱分析证明了碳纤维粉基体上包覆了1层致密均匀而且连续的铁磁性金属镍层,并且没有引入其它杂质元素.通过对包覆前后样品在2～18GHz范围内的复介电常数的实部ε′、虚部系数ε″、复磁导率的实部μ′和虚部系数μ″等电磁参数进行分析比较,可以看出在低频处复合材料的电磁损耗都较纯碳纤维粉有较大提高,可应用于微波吸收材料.
关键词:
化学镀
,
联氨
,
镍
,
电磁参数