金属学报(英文版)
Calcium treatment is nowadays a well-established method to improve steel castability and final properties e.g. machinability, toughness and surface quality. The effects of calcium are mainly based on its strong ability to form sulphides and oxides. The topic of the present paper concerns the basic mechanism and kinetics of the transformation process of alumina inclusions in steel when calcium introduced into the steel e.g. by wire feeding or powder injection.
To clarify the mechanisms model experiments were performed by studying reactions between Al2O3 and CaO in a laboratory furnace as well as by performing Ca treatments in an 8 kg induction furnace for Al deoxidised melt. The phases formed during the reaction between Al2O3 and CaO were examined by SEM-EDS, and the proposed reaction sequence of Al2O3CA6CA2CACAx(liquid) was discussed based on the experimental observations. The kinetics of the reaction of calcium with alumina inclusions were simulated by immersing alumina plates in a Ca treated steel melt in the induction furnace. Results were compared with observations of real inclusion transformation. Based on the results a kinetic model was proposed.
关键词:
Alumina inclusions
,
夹杂
,
机理
,
钙处理
,
动力学
曹树卫
,
孙汝林
,
赵祥梅
,
支艳斌
钢铁研究
针对小规格高速线材生产中出现的颈缩、断丝等现象,分析了生产中辊缝、张力、温度、辊环、导卫等轧制工艺参数设定与调整不当,电气和设备故障,结疤、缩孔、夹杂群等轧件的内外部缺陷等影响因素。讨论了张力设置、高温强度、小断面断丝和断丝受力分析等关键问题,指出机架间张力增大、轧件断面积减小和材料的强度极限降低是产生断丝的根本原因。最后概括了采取的解决措施和应用效果。
关键词:
高速线材
,
颈缩
,
断丝
,
张力
,
结疤
,
缩孔
,
夹杂
郑亮
,
肖程波
,
张国庆
,
袁华
,
韩波
,
唐定中
材料工程
doi:10.3969/j.issn.1001-4381.2012.03.001
对两炉冲击韧性存在明显差异的高Cr铸造镍基高温合金K4648进行了对比研究,通过分析两炉母合金的主量元素和气体含量,采用电子束纽扣锭(EB锭)实验观察合金内夹杂物和对母合金用原材料金属Cr的显微组织分析等方法研究了K4648母合金净度.结果表明:1 #与2#炉批母合金主量元素无明显差别.1 #母合金由于气体元素O含量高达(20.5±7.5)×10-6,远高于2#合金的6×10-6,造成其室温冲击韧性(aku)不及2#合金的一半,低于技术条件要求的19.6J/cm2.电子束纽扣锭(EB锭)实验可有效地将K4648中的夹杂物汇聚,经分析主要是富Y,Ce的氧化物和富Al氧化物.证明高Cr铸造镍基高温合金K4648中添加稀土元素Y,Ce可有效攫取合金中自由态的O和S,生成稳定的稀土氧化物或硫化物,起到净化合金的作用.K4648母合金原材料中金属Cr基体中固溶有15％00(质量分数)的元素O,还分布有富Cr氧化物和Cr,A1,Si的复合氧化物.此外,还存在含N、贫O区域,该区域的维氏显微硬度可达8.2GPa,是Cr基体1.3GPa的6倍,证明N使金属Cr的硬度明显升高.
关键词:
镍基高温合金
,
K4648
,
母合金净度
,
电子束纽扣锭(EB)
,
金属Cr
,
气体含量
,
夹杂
董超群
,
汪治军
,
阎永
,
李崇芊
,
张庆祥
稀有金属
doi:10.3969/j.issn.0258-7076.2003.01.034
通过本文的工艺研究及试验, 使稀土成功地应用于铍铜合金中, 铸锭由于其工艺特点而常出现的气孔、夹杂等缺陷得到了控制, 同时大大提高了合金的综合性能. 稀土对合金的作用与加入量有直接关系, 过多与不及都不好. Cu-RE中间合金在铍铜合金中的最佳加入量为0.1%～0.12%.
关键词:
铍铜合金
,
稀土
,
Cu-RE中间合金
,
气孔
,
夹杂
,
偏析
,
最佳加入量
李涛
,
刘毅
,
郑传奇
表面技术
doi:10.16490/j.cnki.issn.1001-3660.2016.03.007
目的：提高超高强度钢耐海洋大气腐蚀的性能。方法采用周期浸润腐蚀试验箱模拟一般条件下海洋大气腐蚀试验，通过金相显微镜和扫描电子显微镜观察低合金超高强度钢的组织和夹杂物的形貌，采用失重法和电化学阻抗技术分析腐蚀动力学规律及电化学行为规律。结果稀土在低合金超高强度钢中具有细化组织和变质夹杂物的作用，稀土增强了锈层的致密性，使得低合金超高强度钢的耐蚀性能显著提高，且随着稀土含量的增加，锈层电阻值逐渐增大，即稀土提高了锈层对基体的保护能力。结论在低合金超高强度钢中添加稀土能够细化组织、变质夹杂物。稀土低合金超高强度钢的夹杂物主要为球形稀土复合氧硫化物。稀土质量分数为0.08%的低合金超高强度钢的耐腐蚀性能最好。
关键词:
稀土
,
低合金超高强度钢
,
海洋大气腐蚀
,
显微组织
,
夹杂
,
失重法
,
电化学阻抗
杨森祥
钢铁钒钛
简要介绍了攀钢炼钢厂的装备及工艺技术水平,叙述了攀钢近年来为实现洁净钢生产,在铁水预处理、转炉冶炼、钢水精炼(脱硫、脱氧、脱磷及夹杂物控制)等方面所作的改进,以及在350 km/h高速铁路用钢、抗H2S腐蚀石油管坯钢等典型钢种上的应用,实现了wT[0]≤0.001 5％,w[S]≤0.005％,w[P]≤0.010％,氧化物夹杂物级别≤1.0级洁净钢的生产.
关键词:
洁净钢
,
脱硫
,
脱磷
,
夹杂
,
钢轨钢
,
石油管坯钢
宋进英
,
赵远
,
陈连生
,
魏英立
,
田亚强
,
杨栋
钢铁钒钛
doi:10.7513/j.issn.1004-7638.2013.03.022
利用场发射扫描电镜、能谱仪和金相显微镜等检测手段,对冷轧生产中出现的线状缺陷类型及其成因和影响因素进行了分析研究,结果表明常见的线状缺陷主要有气泡类、划伤类、夹杂类及氧化铁皮压入等类型,其中夹杂主要以连铸卷渣为主.并针对常见的线状缺陷提出了转炉炼钢、中间包冶炼、高压水除鳞等环节的工艺改进措施.
关键词:
冷轧板
,
线状缺陷
,
形成原因
,
划伤
,
夹杂
赵新凯
,
李刚利
,
刘西峰
,
鞠伟
物理测试
近几年冷轧带钢的质量异议绝大多数都集中于表面缺陷问题,冷轧带钢表面缺陷形态千变万化,产生原因错综复杂,炼钢、热轧、冷轧之间各工序都可直接或间接造成表面缺陷的产生.文章对唐山建龙实业有限公司冷轧厂低碳铝镇静钢的表面起皮缺陷进行了较为全面的分析.结果表明表面起皮缺陷的原因归结于皮下夹杂和皮下气泡.各工序只有正确识别各种缺陷,加强对缺陷的检测和分析,找到问题的根源,采取相应的措施,才能改善产品质量.
关键词:
冷轧
,
缺陷
,
夹杂
,
气泡
王健春
,
安静
,
丁美英
,
张利平
冶金分析
doi:10.3969/j.issn.1000-7571.2002.01.010
利用TC-436氮氧仪的程序升温功能,研究了一系列光谱纯氧化物试剂Fe2O3,MnO2,NiO,CuO,SiO2,Al2O3以及稀土氧化物La2O3,CeO2等的氧释放曲线;每种氧化物在给定条件下,以跟踪式升温方式受热释放氧,得到了分解温度、分解电流和分解功率.发现不同氧化物分解温度由低到高的顺序为:CuO＜Fe2O3＜NiO＜MnO2＜SiO2＜Al2O3.研究了脱氧纯铁与SiO2或Al2O3混合物的氧状态分析图,模拟钢中夹杂的化学行为.以纯氧化物为参照,做了不同钢种中的氧化物夹杂的氧状态分析,指认了钢中Al系氧化物夹杂的分解峰,部分样品的氧状态分析结果与夹杂分析结果取得了良好的相关性.
关键词:
纯氧化物
,
夹杂
,
跟踪式升温
,
氧状态分析