ZHANG Shaoqing TAO Chunhu Institute of Aeronautical Materials
,
Beijing
,
China.
材料科学技术（英文）
The quench transfomation in a Ti-10V-2Fe-3Al near B-titanium alloy was studied by means of X-ray diffraction, transmission electron microscopy, and optical micyoscopy. The quenching temperatures were above and below the β transus temperature. The phase constitutions of specimens quenched from various solution temperatures were identified and the phase morphologies were examined. In addition, the relationship between phase lattice parameters and quenching tempera- tures was given for α, β and α ~(11) phases. This alloy has a tendency of precipitation of athermal ω phase and formation of stress induced α~(11) mar- tensite from β phase during quenching. Quenched from the temperatures above the β transus tem- perature, the alloy mainly consists of β phase, a small amount of α~(11) martensite and athemal ω phase aye also present in the alloy. After quenching from the temperatures below the β transus temperature, the α phase appeays in the alloy in addition to the phases mentioned above.
关键词:
β-titanium alloy
,
null
,
null
张临财
,
郭啸栋
,
孙巧艳
,
肖林
,
孙军
,
宋振亚
稀有金属材料与工程
对固溶处理后的Ti-10Mo-8V-1Fe-3.5Al (TB3)合金施加弹性压应力,同时在500℃下进行时效处理.TEM观察结果表明:在应力时效的样品里大部分晶粒中α片相互平行排列,即只有一种α片变体,而在未施加压应力常规时效的样品中出现了数种α片的变体.选择了两种强度相当的热处理状态的TB3试样进行低周疲劳测试,一种是500℃自由时效9h,另一种是在约200 MPa压应力下,500℃时效6h.低周疲劳测试结果表明:在同一应变幅下,应力时效试样具有较高的低周疲劳寿命.
关键词:
β钛合金
,
应力时效
,
低周疲劳行为
,
变体选择效应
宋振亚
,
张临财
,
郭啸栋
,
孙巧艳
,
肖林
,
孙军
稀有金属材料与工程
对于经过冷变形的固溶态Ti-10Mo-8V-1Fe-3.5Al (TB3)合金,透射电子显微镜(TEM)观察结果表明:其内部冷变形产生的高密度位错在常规时效后依然大量存在,这将导致合金材料力学性能的劣化.针对此问题,本实验研究了一种二次时效工艺,在常规时效基础上增加了短时间高温时效阶段.TEM观察结果表明,二次时效工艺处理后,合金内部位错密度大幅降低,与此同时时效析出的a片出现了变体选择效应.对经过冷变形及二次时效工艺处理后的TB3合金试样(SA试样)和未变形的常规峰值时效状态试样(FA试样)进行低周轴向拉压疲劳测试结果表明:在总应变幅低于0.01时,SA试样疲劳寿命稍高;总应变幅高于0.01时,FA试样疲劳寿命稍高.另外,对低周疲劳测试后的试样TEM观察结果表明:(1)位错滑移是该合金低周疲劳过程中的主要变形方式；(2)低周疲劳产生的位错条带结构在FA试样中较宽且不连续,而在SA试样中细小均匀.
关键词:
β钛合金
,
预变形
,
二次时效
,
低周疲劳行为
,
变体选择效应
郭强
,
王清
,
韩秀丽
,
鲁学锟
,
孙东立
,
武高辉
稀有金属材料与工程
研究了大变形量冷轧Ti-15-3合金的时效析出行为和时效过程中力学性能的变化.冷变形使Ti-15-3合金中形成部分纳米晶.冷变形合金在450～650℃时效时,从β相纳米晶区析出极为细小的针状α相,而从β相非纳米晶区析出的α相随着时效温度的升高由针状逐渐长大为条状,进而演变为凸透镜状.冷变形合金在450℃时效4 h后,硬度达到了峰值,HV为5328 MPa.450℃时效时在硬度峰值处同样达到了强度峰值,屈服强度和抗拉强度分别可高达1483和1562 MPa.时效温度升高,达到峰值硬度的时间缩短,硬度值大幅度下降.650℃时效后的强度和硬度均低于时效前,粗大的透镜状析出相、纳米晶的长大以及位错密度的急剧下降是650℃时效时硬化效果消失的主要原因.不同时效工艺下的强度和硬度的变化规律相似,性能的变化与时效过程中析出相的状态有关.
关键词:
β钛合金
,
时效
,
α析出相
,
显微硬度
,
力学性能