S.K.He
,
G.S. Wang and S.N. Wang(Beijing institute of Aeronautical Materials
,
Beijing 100095
,
China Manuscript received 26 August 1996)
金属学报(英文版)
Influences of sulphureous impurity and micro-shrinkage on hydrogen assisted cracking (HAC) and fracture behavior of the super-strength low-alloy steel 40CrMnSzMo VA have been studied in this paper.By way of scanning electron microfractography (SEM)and electron probe microanalyser to investigate the fractography of material constantly strained to failure, it was found that the microscopic segregation of sulphureous impurity and micro-shrinkage not only increased strongly the susceptibility to hydrongen embrittlement (HE), but also made the HAC to initiate preferably in such regions with the assistant of stress induced diffusion of hydrogen. The microscopic observation revealed that the steel has commonly intergranular (IG) and quasi-cleavage (QC)features around the segregation of sulphureous impurity and micro-shrinkage for their strong effects of irreversible traps for hydrogen.
关键词:
:micro-shrinkage
,
null
,
null
,
null