Zongyi MA , Yuxiong LU , Ming LUO and Jin BI (Institute of Metal Research , Chinese Academy of Sciences , Shenyang , 110015 , China)Yuzheng ZHANG (Northeastern University Shenyang , 110006 , China)
材料科学技术（英文）
The effects of solution (quench) temperature on the properties of SiCw/Al composite have been investigated using tensile tests. The experiments indicate that the solution temperature of the composite fabricated by P/M technique can be raised to 560℃. The tensile strength of the composite is obviously dependent on solution (quench) temperature and the composite solutionized at 540℃ exhibits a maximum of tensile strength and elongation-to-failure. These results can be accounted for by the variation of the dislocation density in the composite.
关键词:
Zongyi MA , Jihong LI Yuxiong LU , Xiaoguang NING and Jing BI(Lab. of Atomic Imaging of Solids , Institute of Metal Research , Chinese Academy of Sciences , Shenyang 110015 , China)
The in situ formed Al2O3 and TiB2 particulates reinforced Al-3.3 wt pct Cu alloy composite hasbeen successfully fabricated by reaction pressing of TiO2, Al, B and CuO powders. The in situformed Al2O3 and TiB2 particulates with a size from 10 nm to 2 μm are unifOrmly distributedin the matrix. The composite has a tensiIe Strength of 482 MPa and an elastic modulus of103.3 GPa.