Model of Calculating Activity of Nitrogen and Vanadium in FeCVN Molten Metal

PENG Jun , WANG Shijun , DONG Yuanchi , LIU Lixia , ZHOU Yun , CHEN Erbao

钢铁研究学报(英文版)

The solubility of nitrogen in the FeCVN system was measured at 1 708 K and the model of calculating activity (action concentration) of nitrogen (N) and vanadium (V) was derived according to the phase diagram and the coexistence theory of the metal melt structure. The solubility expression of nitrogen in the FeCVN system at 1 708 K was wN=0058 194-0010 367wC+0005 543 4wV. Comparing the computing results with the experimental results, a satisfactory conclusion could be obtained. The analysis of the FeCVN system using this model showed that VN was present in a high temperature metal melt, which would reduce the action concentration of nitrogen obviously. It was consequently disadvantageous to the removal of nitrogen from hot metal.

关键词: metal melt;coexistence theory;action concentration;activity

Thermodynamic Properties of FeCN and FeCBN Melts

CHEN Erbao , WANG Shijun , DONG Yuanchi , WU Baoguo , ZHOU Yun

钢铁研究学报(英文版)

The saturated solubility of carbon and nitrogen in FeCN and FeCBN melts was measured experimentally at 1 485 ℃ to obtain the activity interaction coefficients between components in these melts. A new method was used to treat experimental results. Using thermodynamic derivation and calculation, some important interaction coefficients between components in these melts were obtained.

关键词: FeCN melt;FeCBN melt;FeCB melt;interaction coefficient;thermodynamic property