Effect of Solid Solution Treatment on Microstructure of FeNi Based High Strength Low Thermal Expansion Alloy

ZHANG Jianfu , TU Yifan , XU Jin , ZHANG Jiansheng , ZHANG Jinglin

钢铁研究学报(英文版)

The influence of solid solution treatments on the dissolution of carbides precipitates, the grain size, and the hardness of high strength low expansion alloy were investigated through XRD analysis, microstructure observations, and theoretical computation. It was seen that most primary Mo2C type carbide band dissolved in a temperature range of 1 100-1 150 ℃. When the temperature was over 1 200 ℃, the grain size increased remarkably, which led to the reduction of hardness.

关键词: high strength low expansion alloy;solid solution temperature;microstructure;carbide dissolution