Fe-2Cu-2Ni-1Mo-0.8C (wt pct) elemental mixed powders were rapidly sintered within 6~min by spark plasma sintering, and the effects of sintering parameters on the densification degree and performance of the as-sintered materials were investigated. Results showed that when a proper combination of pulse electric current and constant electric current was employed for sintering, the density and bend strength of the as-sintered material reached the maxima, being 7.61×103 kg/m3 and 1540 MPa, respectively. Its corresponding fracture morphology was characterized as the mix of ductile, intergranular and cleavage fractures.
关键词:
Spark plasma sintering
,
密度
,
组织性能
,
铁基合金