Yanhua LI
材料科学技术（英）
SiCf/Ti-6Al-4V composites were fabricated by the powder-coated fiber method. The precursor fiber was prepared under the optimized parameter, and the composites were made using the vacuum hot pressure method. The influence of heat exposure time on products of the interfacial reaction was investigated using scanning electron microscope (SEM) and analytical transmission electron microscope (TEM) with energy dispersive spectrometer (EDS). The main products are TiC and Ti5Si3 after vacuum exposing the samples at 700℃ for 50 h. The growth dynamics of interfacial reaction products was analyzed quantitatively, which fitted the parabola rule. The activity energy of the reaction was 252 kJ•mol-1.
关键词:
Powder coated fiber
,
null
,
null
,
null
,
null
Yanhua LI
,
Nanlin SHI
,
Dezhi ZHANG
,
Rui YANG
材料科学技术（英）
A continuous loading push-out test technique was used to measure the interfacial shear strength of SiC fiber reinforced Ti matrix composites. The interfacial shear strength of samples as-fabricated and after heat exposed at 700 and 800℃ for 50 h was successfully determined. It has been found that the interfacial shear strength of the specimen exposed at 700℃ was higher than that of as-prepared and exposed samples at 800℃. The shear strength of the as-prepared samples was about 112.45 MPa, and increased to about 153.77 MPa after heat-treating at 700℃ for 50 h, but decreased to 133.11 MPa after treating at 800℃ for 50 h. Scanning electron microscope (SEM) was used to investigate the interfacial morphology of the samples. The brittle phase was the main products of interface for samples exposed at 800℃, and the interface was easily peeled off.
关键词:
Push-out test
,
null
,
null
,
null